Formation Wear Resistant Coatings on Martensite Steel Hardox 450 by Welding Methods
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 142 : Innovative Technologies in Engineering.— 2016.— [012079, 6 p.] |
|---|---|
| Autor Corporativo: | |
| Outros autores: | , , , , |
| Summary: | Title screen By methods of modern physical materials science the investigations analysis of phase composition, defect substructure, mechanical and tribological properties of Cr-Nb-C-V containing coatings formed in surfacing on martensitic wear resistant steel Hardox 450 were carried out. It was shown that surfacing resulted in the formation of high strength surface layer 6 mm in thinness. This layer had wear resistance 138 times greater than that of the base and friction coefficient 2.5 times less. Having analyzed the deflected mode of the deposited material in conditions of friction, a conclusion is drawn that plastic shear deformation is localized in the surface layer due to the high friction factor, as the result, scratches are formed. The maximum of tangential stress is deflected deep into the material provided that friction factor is low. On the basis of the investigations by methods of X-ray structural analysis and transmission diffraction electron microscopy it was shown that increase strength and tribological properties of surfacing metal were caused by its phase composition and state of defect substructure, namely, availability of interstitial phases (more than 36%) and martensitic type of a-phase structure. |
| Publicado: |
2016
|
| Subjects: | |
| Acceso en liña: | http://dx.doi.org/10.1088/1757-899X/142/1/012079 http://earchive.tpu.ru/handle/11683/34754 |
| Formato: | Electrónico Capítulo de libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=650445 |
| Summary: | Title screen By methods of modern physical materials science the investigations analysis of phase composition, defect substructure, mechanical and tribological properties of Cr-Nb-C-V containing coatings formed in surfacing on martensitic wear resistant steel Hardox 450 were carried out. It was shown that surfacing resulted in the formation of high strength surface layer 6 mm in thinness. This layer had wear resistance 138 times greater than that of the base and friction coefficient 2.5 times less. Having analyzed the deflected mode of the deposited material in conditions of friction, a conclusion is drawn that plastic shear deformation is localized in the surface layer due to the high friction factor, as the result, scratches are formed. The maximum of tangential stress is deflected deep into the material provided that friction factor is low. On the basis of the investigations by methods of X-ray structural analysis and transmission diffraction electron microscopy it was shown that increase strength and tribological properties of surfacing metal were caused by its phase composition and state of defect substructure, namely, availability of interstitial phases (more than 36%) and martensitic type of a-phase structure. |
|---|---|
| DOI: | 10.1088/1757-899X/142/1/012079 |