Structural Evolution and Mechanical Properties of a VT22 Titanium Alloy Under High-Temperature Deformation; Russian Physics Journal; Vol. 59, № 3

Structural Evolution and Mechanical Properties of a VT22 Titanium Alloy Under High-Temperature Deformation; Russian Physics Journal; Vol. 59, № 3

Détails bibliographiques
Parent link:Russian Physics Journal.— , 1965-
Vol. 59, № 3.— 2016.— [P. 397–402]
Collectivité auteur: Национальный исследовательский Томский политехнический университет Физико-технический институт Лаборатория радиационного контроля № 31
Autres auteurs: Ratochka L. V. Iljya Vasiljevich, Mishin I. P. Ivan Petrovich, Lykova O. P. Olga Nikolaevna, Naydenkin E. V. Evgeny Vladimirovich, Varlamova N. V. Natalya Valeryevna
Résumé:Title screen
The special features inherent in the development of high-temperature deformation and structural evolution in materials are investigated, using a VT22 titanium alloy of the transition class (Ti - 4.74 mass% Al - 5.57 mass% Mo - 5.04 mass% V) subjected to helical rolling + aging as an example. This treatment is found to give rise to an intragrain fine acicular martensite structure with fine inclusions of α-phase particles of size ~1 μm. It is shown that in the alloy undergoing plastic deformation at temperatures approaching the polymorphic transformation temperature, the elongation to failure is in excess of 300%. The high plasticity of the alloy in the conditions considered is likely to be due to vigorous development of phase transformations and intensification of diffusion-controlled processes, including the effects of the evolution of the dislocation structure, growth of subgrains, and formation of new grains in the bulk of the pre-existing ones during plastic deformation.
Режим доступа: по договору с организацией-держателем ресурса
Langue:anglais
Publié: 2016
Sujets:
электронный ресурс
труды учёных ТПУ
Accès en ligne:http://dx.doi.org/10.1007/s11182-016-0786-8
Format: Électronique Chapitre de livre
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=650287

Documents similaires

Documents similaires