Porous Ceramics Obtained with the Use of Aluminum Hydroxide Powder; Oriental journal of chemistry; Vol. 31, № 1
| Parent link: | Oriental journal of chemistry: Research Journal Vol. 31, № 1.— 2015.— [P. 93-100] |
|---|---|
| Autor corporatiu: | |
| Altres autors: | , , , , , , |
| Sumari: | Title screen This work was aimed at studying the influence of structure and properties of powders of aluminum hydroxide and zirconium dioxide on the structure and properties of the obtained ceramics. The work studied Al2O3ceramics obtained from aluminum hydroxide and composite materials ZrO2-Al2O3 obtained from mixtures of zirconium dioxide and aluminum hydroxide powders. The work shows the data about the structure and properties of the initial powders used for the production of ceramics, as well as data about the structure and properties of Al2O3and ZrO2-Al2O3 ceramic materials. It has been found that increasing aluminum hydroxide content in the initial mixture with the zirconium dioxide powder leads to increasing porosity of ZrO2-Al2O3 composites sintered within the temperature range between 1,400 and 1,650 °C. It has been shown that increasing sintering temperature of the Al2O3ceramics leads to increasing compressive strength from 6 MPa to 800 MPa at the temperature of sintering between 1,300 and 1,500 °C, respectively. |
| Idioma: | anglès |
| Publicat: |
2015
|
| Matèries: | |
| Accés en línia: | http://dx.doi.org/10.13005/ojc/320109 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=649239 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 649239 | ||
| 005 | 20250303143935.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\14401 | ||
| 035 | |a RU\TPU\network\9762 | ||
| 090 | |a 649239 | ||
| 100 | |a 20160627d2015 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a IN | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Porous Ceramics Obtained with the Use of Aluminum Hydroxide Powder |f I. A. Zhukov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 99-100 (21 tit.)] | ||
| 330 | |a This work was aimed at studying the influence of structure and properties of powders of aluminum hydroxide and zirconium dioxide on the structure and properties of the obtained ceramics. The work studied Al2O3ceramics obtained from aluminum hydroxide and composite materials ZrO2-Al2O3 obtained from mixtures of zirconium dioxide and aluminum hydroxide powders. The work shows the data about the structure and properties of the initial powders used for the production of ceramics, as well as data about the structure and properties of Al2O3and ZrO2-Al2O3 ceramic materials. It has been found that increasing aluminum hydroxide content in the initial mixture with the zirconium dioxide powder leads to increasing porosity of ZrO2-Al2O3 composites sintered within the temperature range between 1,400 and 1,650 °C. It has been shown that increasing sintering temperature of the Al2O3ceramics leads to increasing compressive strength from 6 MPa to 800 MPa at the temperature of sintering between 1,300 and 1,500 °C, respectively. | ||
| 461 | |t Oriental journal of chemistry |o Research Journal | ||
| 463 | |t Vol. 31, № 1 |v [P. 93-100] |d 2015 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a оксид алюминия | |
| 610 | 1 | |a гидрооксид алюминия | |
| 610 | 1 | |a диоксид циркония | |
| 610 | 1 | |a прочность | |
| 610 | 1 | |a композиты | |
| 701 | 1 | |a Zhukov |b I. A. |g Iljya Aleksandrovich | |
| 701 | 1 | |a Dedova |b E. S. |c specialist in the field of material science |c Assistant of the Department of Tomsk Polytechnic University |f 1987- |g Elena Sergeevna |3 (RuTPU)RU\TPU\pers\34676 |9 18026 | |
| 701 | 1 | |a Buyakova |b S. P. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1968- |g Svetlana Petrovna |3 (RuTPU)RU\TPU\pers\34758 |9 18108 | |
| 701 | 1 | |a Kulkov |b S. N. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1952-2021 |g Sergey Nikolaevich |3 (RuTPU)RU\TPU\pers\31428 |9 15591 | |
| 701 | 1 | |a Levkov |b R. V. |g Ruslan Viktorovich | |
| 701 | 1 | |a Mamontov |b G. V. |g Grigory Vladimirovich | |
| 701 | 1 | |a Promakhov |b V. V. |g Vladimir Vasiljevich | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Институт физики высоких технологий |b Кафедра материаловедения в машиностроении |3 (RuTPU)RU\TPU\col\18688 |9 27141 |
| 801 | 2 | |a RU |b 63413507 |c 20160627 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.13005/ojc/320109 | |
| 942 | |c CF | ||