Flexible antibacterial Zr-Cu-N thin films resistant to cracking; Journal of Vacuum Science and Technology A; Vol. 34, iss. 2
| Parent link: | Journal of Vacuum Science and Technology A Vol. 34, iss. 2.— 2015.— [7 p.] |
|---|---|
| Співавтор: | |
| Інші автори: | , , , |
| Резюме: | Title screen This study investigates how the Cu concentration in Zr-Cu-N films affects the films' antibacterial capacity and mechanical properties. Zr-Cu-N films were prepared by reactive magnetron sputtering from composed Zr/Cu targets using a dual magnetron in an Ar + N2 mixture. The antibacterial capacity of Zr-Cu-N films was tested on Escherichia coli (E. coli) bacteria. The mechanical properties of Zr-Cu-N filmswere determined from the load vs. displacement curves measured using a Fisherscope H 100microhardness tester. The antibacterial capacity was modulated by the amount of Cu added to the Zr-Cu-N film. The mechanical properties were varied based on the energy Ei delivered to the growing film by bombarding ions. It was found that it is possible to form Zr-Cu-N films with Cu concentrations ≥10 at. % that simultaneously exhibit (1) 100% killing efficiency Ek for E. colibacteria on their surfaces, and (2) (1) high hardness H of about 25 GPa, (2) high ratio H/E* ≥ 0.1, (3) high elastic recovery We ≥ 60% and (4) compressive macrostress (σ < 0). The Zr-Cu-N films with these parameters are flexible/antibacterial filmsthat exhibit enhanced resistance to cracking. This enhanced resistance was tested by (1) bending the Mo and Ti strip coated by sputtered Zr-Cu-N films (bending test) and (2) loading the surface of the Zr-Cu-Nsputtered on a Si substrate by a diamond indenter at high loads up to 1 N (indentation test). Physical, mechanical, and antibacterial properties of Zr-Cu-N films are described in detail. In summary, it can be concluded that Zr-Cu-N is a promising new material for creating flexible antibacterial coatings on contact surfaces. Режим доступа: по договору с организацией-держателем ресурса |
| Мова: | Англійська |
| Опубліковано: |
2015
|
| Предмети: | |
| Онлайн доступ: | http://dx.doi.org/10.1116/1.4937727 |
| Формат: | Електронний ресурс Частина з книги |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=649150 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 649150 | ||
| 005 | 20250228154939.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\14311 | ||
| 035 | |a RU\TPU\network\14301 | ||
| 090 | |a 649150 | ||
| 100 | |a 20160622d2016 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Flexible antibacterial Zr-Cu-N thin films resistant to cracking |f Y. Musil [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 40 tit.] | ||
| 330 | |a This study investigates how the Cu concentration in Zr-Cu-N films affects the films' antibacterial capacity and mechanical properties. Zr-Cu-N films were prepared by reactive magnetron sputtering from composed Zr/Cu targets using a dual magnetron in an Ar + N2 mixture. The antibacterial capacity of Zr-Cu-N films was tested on Escherichia coli (E. coli) bacteria. The mechanical properties of Zr-Cu-N filmswere determined from the load vs. displacement curves measured using a Fisherscope H 100microhardness tester. The antibacterial capacity was modulated by the amount of Cu added to the Zr-Cu-N film. The mechanical properties were varied based on the energy Ei delivered to the growing film by bombarding ions. It was found that it is possible to form Zr-Cu-N films with Cu concentrations ≥10 at. % that simultaneously exhibit (1) 100% killing efficiency Ek for E. colibacteria on their surfaces, and (2) (1) high hardness H of about 25 GPa, (2) high ratio H/E* ≥ 0.1, (3) high elastic recovery We ≥ 60% and (4) compressive macrostress (σ < 0). The Zr-Cu-N films with these parameters are flexible/antibacterial filmsthat exhibit enhanced resistance to cracking. This enhanced resistance was tested by (1) bending the Mo and Ti strip coated by sputtered Zr-Cu-N films (bending test) and (2) loading the surface of the Zr-Cu-Nsputtered on a Si substrate by a diamond indenter at high loads up to 1 N (indentation test). Physical, mechanical, and antibacterial properties of Zr-Cu-N films are described in detail. In summary, it can be concluded that Zr-Cu-N is a promising new material for creating flexible antibacterial coatings on contact surfaces. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Journal of Vacuum Science and Technology A | ||
| 463 | |t Vol. 34, iss. 2 |v [7 p.] |d 2015 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 701 | 1 | |a Musil |b Y. |c physicist |c Leading researcher of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1934- |g Yindrikh |3 (RuTPU)RU\TPU\pers\36957 |9 19976 | |
| 701 | 1 | |a Zitek |b M. |g Michal | |
| 701 | 1 | |a Fajfrlik |b K. |g Karel | |
| 701 | 1 | |a Cerstvy |b R. |g Radomir | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Институт физики высоких технологий |b Лаборатория № 1 |3 (RuTPU)RU\TPU\col\19035 |9 27311 |
| 801 | 2 | |a RU |b 63413507 |c 20160622 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1116/1.4937727 | |
| 942 | |c CF | ||