Application of a low-pressure arc discharge for formation of hard diffusion surface layers

Application of a low-pressure arc discharge for formation of hard diffusion surface layers

Bibliografiset tiedot
Parent link:Discharges and Electrical Insulation in Vacuum: XXIst International Symposium. [P. 583-586].— , 2004
Muut tekijät: Koval N. N. Nikolay Nikolaevich, Grigoriev S. V., Ivanov Yu. F. Yuriy Fedorovich, Lopatin I. V., Strumilova Т. V., Shirinkina A. V.
Yhteenveto:Title screen
Investigations of surface modification of structural and tool steels treated in low-pressure arc discharges plasmas have been carried out. The complex treatment in single vacuum cycle involved a sequence of operations: ion cleaning of the surface and heating the sample, diffusion surface alloying with aluminum and nitriding. The sample temperature was not over 620°C at all stages of the process and the total time of treatment was approximately 2 hr. The structure, phase and element constitution, and microhardness of the surface layer have been investigated. It has been established that the significant increase in microhardness from 2-1.5 in the original state to 10-13 GPa in the modified layer after complex diffusion saturation in an arc discharge is due to the formation of iron nitride containing dispersed particles of aluminum nitride.
Режим доступа: по договору с организацией-держателем ресурса
Kieli:englanti
Julkaistu: 2004
Aiheet:
электронный ресурс
труды учёных ТПУ
взаимодействия с лазерным лучом
тонкое пленочное покрытие
Linkit:http://dx.doi.org/10.1109/DEIV.2004.1422683
Aineistotyyppi: Elektroninen Kirjan osa
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=648663

Samankaltaisia teoksia

Samankaltaisia teoksia