The character of fracture of iron based thermal coating during fretting
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 124 : Mechanical Engineering, Automation and Control Systems (MEACS2015).— 2016.— [012126, 4 p.] |
|---|---|
| Autore principale: | |
| Ente Autore: | |
| Altri autori: | , |
| Riassunto: | Title screen The character of destruction of thermal coatings during fretting has been investigated. An iron based plasma coating has been tested with oscillation amplitude from 30 to 200 microns. The tests were conducted in air. It has been determined that the main factor influencing the rate of the wear of the coating during fretting corrosion is the size of the coating area involved into the wear process. The coating exhibits high wear resistance when the amplitude of the oscillation is commensurate with the size of the sprayed particles. During destruction of the coating the leading role belongs to fatigue-oxidation processes. The wear of the coating acquires a catastrophic character when coating macro defects - pores and interlayer boundaries - are involved into the wear process. |
| Pubblicazione: |
2016
|
| Serie: | Materials Science in Mechanical Engineering |
| Soggetti: | |
| Accesso online: | http://dx.doi.org/10.1088/1757-899X/124/1/012126 http://earchive.tpu.ru/handle/11683/33885 |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=648599 |
| Riassunto: | Title screen The character of destruction of thermal coatings during fretting has been investigated. An iron based plasma coating has been tested with oscillation amplitude from 30 to 200 microns. The tests were conducted in air. It has been determined that the main factor influencing the rate of the wear of the coating during fretting corrosion is the size of the coating area involved into the wear process. The coating exhibits high wear resistance when the amplitude of the oscillation is commensurate with the size of the sprayed particles. During destruction of the coating the leading role belongs to fatigue-oxidation processes. The wear of the coating acquires a catastrophic character when coating macro defects - pores and interlayer boundaries - are involved into the wear process. |
|---|---|
| DOI: | 10.1088/1757-899X/124/1/012126 |