Properties of Foam Glass Material Modified by Nanosize Zirconium Dioxide; Glass and Ceramics; Vol. 73, iss. 1
| Parent link: | Glass and Ceramics Vol. 73, iss. 1.— 2016.— [P. 39-42] |
|---|---|
| Enti autori: | , |
| Altri autori: | , , , |
| Riassunto: | Title screen The effect of small additions of zirconium concentrate with average particle size 30 nm on the physical and mechanical properties of foam glass is examined. It is found that the introduction of zirconium dioxide into the foaming mixture changes the macrostructure of foam glass and increases the average pore size to 2.5 mm. Nanosize ZrO2 decreases the viscosity of melt upon foaming. The optimal weight content of zirconium dioxide from the standpoint of mechanical properties is 0.3 wt.%. The strength of foam glass increases in the presence of nanosize particles to 1.4 MPa compared with the strength of the initial material 1.1 MPa. Subsequent increase of the zirconium dioxide content to 1.1 wt.% decreases the strength to 0.5 MPa. Режим доступа: по договору с организацией-держателем ресурса |
| Lingua: | inglese |
| Pubblicazione: |
2016
|
| Soggetti: | |
| Accesso online: | http://dx.doi.org/10.1007/s10717-016-9821-z |
| Natura: | MixedMaterials Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=648546 |