General regularities of the microstructure formation during friction stir welding and sliding friction; Journal of Friction and Wear; Vol. 36, iss. 2
| Parent link: | Journal of Friction and Wear: Scientific Journal Vol. 36, iss. 2.— 2015.— [P. 127-131] |
|---|---|
| निगमित लेखक: | |
| अन्य लेखक: | , , , , , , |
| सारांश: | Title screen A comparative metallographic analysis of the formation of the metal microstructure during sliding friction and friction stir welding is performed. It has been shown based on the example of a weld joint made of aluminum alloy fabricated by friction stir welding that the weld microstructure has all signs of the deformed layer of metal formed due to sliding friction, which is accompanied by the seizure of conjugated surfaces. Режим доступа: по договору с организацией-держателем ресурса |
| भाषा: | अंग्रेज़ी |
| प्रकाशित: |
2015
|
| विषय: | |
| ऑनलाइन पहुंच: | http://dx.doi.org/10.3103/S1068366615020087 |
| स्वरूप: | इलेक्ट्रोनिक पुस्तक अध्याय |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=647882 |
| सारांश: | Title screen A comparative metallographic analysis of the formation of the metal microstructure during sliding friction and friction stir welding is performed. It has been shown based on the example of a weld joint made of aluminum alloy fabricated by friction stir welding that the weld microstructure has all signs of the deformed layer of metal formed due to sliding friction, which is accompanied by the seizure of conjugated surfaces. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| डिजिटल ऑब्जेक्ट पहचानकर्ता: | 10.3103/S1068366615020087 |