Influence of Anodization Time and Voltage on the Parameters of TiO[2] Nanotubes; IOP Conference Series: Materials Science and Engineering; Vol. 116 : Advanced Materials and New Technologies in Modern Materials Science
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 116 : Advanced Materials and New Technologies in Modern Materials Science.— 2016.— [012025, 6 p.] |
|---|---|
| Autor principal: | |
| Autor Corporativo: | |
| Outros Autores: | , |
| Resumo: | Title screen A vertically aligned titania nanotube layer was obtained by electrochemical anodic oxidation in the electrolyte contained 0.4 wt% solution of NH[4]F in 54 ml of ethylene glycol and 5 ml of deionized water, after titanium was chemically cleaned/etched with a mixture of HCl, H[2]O and HNO[3] solution for removing the natural oxide films. The morphology and composition of the titania nanotube layer were examined by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). The anodization of TiO[2] nanotubes was done using 60 V for 240 min and 30 min, and 30 V for 30 min. The diameter of the titania nanotubes was about 52-156 nm, the wall thickness about 32-53 nm and the height about 0.9-6.3 [mu]m. The pore size of TiO[2] nanotubes influences the dissolution rate of CaP thin films and Young's modulus, which is significantly lower than that of the Ti substrate. Our future challenge will be investigation of the microstructure and mechanical behavior of titania nanotubes with CaP film. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | inglês |
| Publicado em: |
2016
|
| Assuntos: | |
| Acesso em linha: | http://dx.doi.org/10.1088/1757-899X/116/1/012025 http://earchive.tpu.ru/handle/11683/18926 |
| Formato: | Recurso Eletrônico Capítulo de Livro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=647106 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 647106 | ||
| 005 | 20250826095554.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\12243 | ||
| 035 | |a RU\TPU\network\12242 | ||
| 090 | |a 647106 | ||
| 100 | |a 20160325a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Influence of Anodization Time and Voltage on the Parameters of TiO[2] Nanotubes |f R. V. Chernozem, M. A. Surmeneva, R. A. Surmenev | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 6 tit.] | ||
| 330 | |a A vertically aligned titania nanotube layer was obtained by electrochemical anodic oxidation in the electrolyte contained 0.4 wt% solution of NH[4]F in 54 ml of ethylene glycol and 5 ml of deionized water, after titanium was chemically cleaned/etched with a mixture of HCl, H[2]O and HNO[3] solution for removing the natural oxide films. The morphology and composition of the titania nanotube layer were examined by scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). The anodization of TiO[2] nanotubes was done using 60 V for 240 min and 30 min, and 30 V for 30 min. The diameter of the titania nanotubes was about 52-156 nm, the wall thickness about 32-53 nm and the height about 0.9-6.3 [mu]m. The pore size of TiO[2] nanotubes influences the dissolution rate of CaP thin films and Young's modulus, which is significantly lower than that of the Ti substrate. Our future challenge will be investigation of the microstructure and mechanical behavior of titania nanotubes with CaP film. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\2008 |t IOP Conference Series: Materials Science and Engineering | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\11962 |t Vol. 116 : Advanced Materials and New Technologies in Modern Materials Science |o International Conference, 9–11 November 2015, Tomsk, Russia |o [proceedings] |v [012025, 6 p.] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a анодирование | |
| 610 | 1 | |a напряжения | |
| 610 | 1 | |a нанотрубки | |
| 610 | 1 | |a диоксид титана | |
| 610 | 1 | |a пленки | |
| 700 | 1 | |a Chernozem |b R. V. |c physicist |c Associate Professor of Tomsk Polytechnic University |f 1992- |g Roman Viktorovich |3 (RuTPU)RU\TPU\pers\36450 |9 19499 | |
| 701 | 1 | |a Surmeneva |b M. A. |c specialist in the field of material science |c engineer-researcher of Tomsk Polytechnic University, Associate Scientist |f 1984- |g Maria Alexandrovna |3 (RuTPU)RU\TPU\pers\31894 |9 15966 | |
| 701 | 1 | |a Surmenev |b R. A. |c physicist |c Associate Professor of Tomsk Polytechnic University, Senior researcher, Candidate of physical and mathematical sciences |f 1982- |g Roman Anatolievich |3 (RuTPU)RU\TPU\pers\31885 |9 15957 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Физико-технический институт (ФТИ) |b Кафедра теоретической и экспериментальной физики (ТиЭФ) |b Центр технологий (ЦТ) |3 (RuTPU)RU\TPU\col\20620 |
| 801 | 2 | |a RU |b 63413507 |c 20161215 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1088/1757-899X/116/1/012025 | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18926 | |
| 942 | |c CF | ||