The influence of nickel layer thickness on microhardness and hydrogen sorption rate of commercially pure titanium alloy
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 110 : Radiation-Thermal Effects and Processes in Inorganic Materials (RTEP2015).— 2016.— [012071, 5 p.] |
|---|---|
| Müşterek Yazar: | |
| Diğer Yazarlar: | , , , |
| Özet: | Title screen The influence of nickel coating thickness on microhardness and hydrogen sorption rate by commercially pure titanium alloy was established in this work. Coating deposition was carried out by magnetron sputtering method with prior ion cleaning of surface. It was shown that increase of sputtering time from 10 to 50 minutes leads to increase coating thickness from 0.56 to 3.78 μm. It was established that increase of nickel coating thickness leads to increase of microhardness at loads less than 0.5 kg. Microhardness values for all samples are not significantly different at loads 1 kg. Hydrogen content in titanium alloy with nickel layer deposited at 10 and 20 minutes exceeds concentration in initial samples on one order of magnitude. Further increasing of deposition time of nickel coating leads to decreasing of hydrogen concentration in samples due to coating delamination in process of hydrogenation. Режим доступа: по договору с организацией-держателем ресурса |
| Dil: | İngilizce |
| Baskı/Yayın Bilgisi: |
2016
|
| Konular: | |
| Online Erişim: | http://dx.doi.org/10.1088/1757-899X/110/1/012071 http://earchive.tpu.ru/handle/11683/18082 |
| Materyal Türü: | Elektronik Kitap Bölümü |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=647040 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 647040 | ||
| 005 | 20251122071714.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\12177 | ||
| 035 | |a RU\TPU\network\12176 | ||
| 090 | |a 647040 | ||
| 100 | |a 20160324a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a The influence of nickel layer thickness on microhardness and hydrogen sorption rate of commercially pure titanium alloy |f V. N. Kudiyarov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 15 tit.] | ||
| 330 | |a The influence of nickel coating thickness on microhardness and hydrogen sorption rate by commercially pure titanium alloy was established in this work. Coating deposition was carried out by magnetron sputtering method with prior ion cleaning of surface. It was shown that increase of sputtering time from 10 to 50 minutes leads to increase coating thickness from 0.56 to 3.78 μm. It was established that increase of nickel coating thickness leads to increase of microhardness at loads less than 0.5 kg. Microhardness values for all samples are not significantly different at loads 1 kg. Hydrogen content in titanium alloy with nickel layer deposited at 10 and 20 minutes exceeds concentration in initial samples on one order of magnitude. Further increasing of deposition time of nickel coating leads to decreasing of hydrogen concentration in samples due to coating delamination in process of hydrogenation. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\2008 |t IOP Conference Series: Materials Science and Engineering | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\11965 |t Vol. 110 : Radiation-Thermal Effects and Processes in Inorganic Materials (RTEP2015) |o International Scientific Conference, 31 August to 10 September 2015, Tomsk, Russia |o [proceedings] |v [012071, 5 p.] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a слои | |
| 610 | 1 | |a никель | |
| 610 | 1 | |a микротвердость | |
| 610 | 1 | |a сорбция | |
| 610 | 1 | |a водород | |
| 610 | 1 | |a титановые сплавы | |
| 701 | 1 | |a Kudiyarov |b V. N. |c physicist |c Associate Professor of Tomsk Polytechnic University, Candidate of Technical Sciences |f 1990- |g Victor Nikolaevich |y Tomsk |3 (RuTPU)RU\TPU\pers\30836 |9 15083 | |
| 701 | 1 | |a Kashkarov |b E. B. |c Physicist |c Associate Professor, Researcher of Tomsk Polytechnic University, Candidate of Physical and Mathematical Sciences |f 1991- |g Egor Borisovich |3 (RuTPU)RU\TPU\pers\34949 |9 18267 | |
| 701 | 1 | |a Syrtanov |b M. S. |c physicist |c Associate Professor, Researcher of Tomsk Polytechnic University, Candidate of Technical Sciences |f 1990- |g Maksim Sergeevich |3 (RuTPU)RU\TPU\pers\34764 |9 18114 | |
| 701 | 1 | |a Yugova |b I. S. | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Физико-технический институт (ФТИ) |b Кафедра общей физики (ОФ) |3 (RuTPU)RU\TPU\col\18734 |
| 801 | 2 | |a RU |b 63413507 |c 20161121 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1088/1757-899X/110/1/012071 | |
| 856 | 4 | 0 | |u http://earchive.tpu.ru/handle/11683/18082 |
| 942 | |c CF | ||