Hydrogen Concentration Measurements at Titanium Layers by Means of Thermo-EMF; Key Engineering Materials; Vol. 683 : Multifunctional Materials: Development and Application
| Parent link: | Key Engineering Materials: Scientific Journal Vol. 683 : Multifunctional Materials: Development and Application.— 2016.— [P. 199-202] |
|---|---|
| Hlavní autor: | |
| Korporativní autor: | |
| Další autoři: | , |
| Shrnutí: | Title screen The thermo-emf and electrical resistivity of hydrogenated titanium were measured. Hydrogen concentration in titanium varies from 0.005 to 0.25%. We have compared the methods regarding their sensitivity to the alteration of thermo-emf and electrical resistivity during titanium hydrogenation. The accuracy of the obtained results was verified by comparing them with the results for palladium. It was demonstrated that the method implementing thermo-emf is sensitive to hydrogen concentration in titanium at different depth of the alloy. On the basis of performed measurements, we have proposed a graphical method for detecting the change in titanium structure. Режим доступа: по договору с организацией-держателем ресурса |
| Jazyk: | angličtina |
| Vydáno: |
2016
|
| Edice: | Physicochemical Properties of Materials and Current Processing Technologies |
| Témata: | |
| On-line přístup: | http://dx.doi.org/10.4028/www.scientific.net/KEM.683.199 |
| Médium: | MixedMaterials Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=646607 |
| Shrnutí: | Title screen The thermo-emf and electrical resistivity of hydrogenated titanium were measured. Hydrogen concentration in titanium varies from 0.005 to 0.25%. We have compared the methods regarding their sensitivity to the alteration of thermo-emf and electrical resistivity during titanium hydrogenation. The accuracy of the obtained results was verified by comparing them with the results for palladium. It was demonstrated that the method implementing thermo-emf is sensitive to hydrogen concentration in titanium at different depth of the alloy. On the basis of performed measurements, we have proposed a graphical method for detecting the change in titanium structure. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.4028/www.scientific.net/KEM.683.199 |