Chromium Alloyed Steel Nitriding within Close-To-Critical Temperature Range; Advanced Materials Research; Vol. 1013 : Structure and Properties of Metals at DifferentEnergy Effects and Treatment Technologies
| Parent link: | Advanced Materials Research: Scientific Journal Vol. 1013 : Structure and Properties of Metals at DifferentEnergy Effects and Treatment Technologies.— 2014.— [P. 146-152] |
|---|---|
| Collectivité auteur: | |
| Autres auteurs: | , , , , |
| Résumé: | Title screen The paper presents X-ray diffraction and scanning electron microscope analyses, and durometer measurements used to investigate the structural properties and phase composition of nitride layers of type 20Kh13 mild steel. A method of nitriding by low-pressure arc discharge was applied along with the combined surface treatment including ultrasonic finishing and nitriding. It was shown that within the close-to-critical temperature range starting from 200oС, the nitride layers was formed on the surface of type 20Kh13 mild steel. The ultrasonic pre-treatment shown its effect on the steel nitriding that increased the amount of nitride phases and the value of microharness on the steel surface. Режим доступа: по договору с организацией-держателем ресурса |
| Langue: | anglais |
| Publié: |
2014
|
| Sujets: | |
| Accès en ligne: | http://dx.doi.org/10.4028/www.scientific.net/AMR.1013.146 |
| Format: | Électronique Chapitre de livre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=646455 |