Properties and structural state of the surface layer in a zirconium alloy modified by a pulsed electron beam and saturated by hydrogen; Technical Physics; Vol. 57, iss. 3

Մատենագիտական մանրամասներ
Parent link:	Technical Physics Vol. 57, iss. 3.— 2012.— [P. 392-398]
Այլ հեղինակներ:	Chernov I. P. Ivan Petrovich, Ivanova S. V. Svetlana Vladimirovna, Kroening H. M. V. A. Hans Michael Wilhelm Adolf, Koval N. N. Nikolay Nikolaevich, Larionov V. V. Vitaliy Vasilyevich, Lider A. M. Andrey Markovich, Pushilina N. S. Natalia Sergeevna, Stepanova E. N. Ekaterina Nikolaevna, Stepanova O. M. Olga Mikhailovna, Cherdantsev Yu. P. Yuriy Petrovich
Ամփոփում:	Title screen A pulsed action of an electron beam on a Zr-1% Nb zirconium alloy is studied. Alloy samples are irradiated by three 50-μs pulses at an energy density of 15-25 J/cm 2, a power of (3-6) × 10 4 W/cm 2, a current density of 10-50 A/cm 2, and an electron energy of 18 keV. This method of processing is found to modify the surface layer of the alloy without changing the structure-phase state of its volume. This surface modification increases the hydrogen saturation resistance of the alloy. Режим доступа: по договору с организацией-держателем ресурса
Լեզու:	անգլերեն
Հրապարակվել է:	2012
Շարք:	Solid State
Խորագրեր:	труды учёных ТПУ
Առցանց հասանելիություն:	http://dx.doi.org/10.1134/S1063784212030024
Ձևաչափ:	Էլեկտրոնային Գրքի գլուխ
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=645875

Համացանց