Деформационное поведение технически чистого титана, подвергнутого ультразвуковой обработке и последующему растяжению
| Parent link: | Деформация и разрушение материалов и наноматериалов.— 2015.— [С. 114-115] |
|---|---|
| Erakunde egilea: | |
| Beste egile batzuk: | , , , , , |
| Gaia: | Заглавие с экрана In this work the effect of ultrasonic treatment of commercial purity titanium on its deformationbehavior under uniaxial quasi-static tension was studied. Multilevel character of plastic deformation ofcommercial purity titanium surface-hardened layers was demonstrated. It was shown that during tension coarseslip bands developed intensively in surface grains of titanium specimens. These slip bands freely cross twinsformed during ultrasonic treatment that resulting in secondary twinning. |
| Hizkuntza: | errusiera |
| Argitaratua: |
2015
|
| Gaiak: | |
| Sarrera elektronikoa: | http://files.imetran.ru/SbornikDFMN/Sbornik_DFMN2015.pdf#page=114 |
| Formatua: | Baliabide elektronikoa Liburu kapitulua |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=645754 |
| Gaia: | Заглавие с экрана In this work the effect of ultrasonic treatment of commercial purity titanium on its deformationbehavior under uniaxial quasi-static tension was studied. Multilevel character of plastic deformation ofcommercial purity titanium surface-hardened layers was demonstrated. It was shown that during tension coarseslip bands developed intensively in surface grains of titanium specimens. These slip bands freely cross twinsformed during ultrasonic treatment that resulting in secondary twinning. |
|---|