The Distinctive Feature of Weld Joints Structure by Adding the Nanomodifying to the Weld Pool; AIP Conference Proceedings; Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures
| Parent link: | AIP Conference Proceedings Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures.— 2015.— [020210, 4 p.] |
|---|---|
| Korporativní autor: | |
| Další autoři: | , , , , |
| Shrnutí: | Title screen The experimental studies were carried on for the test samples of welds of the steel 12X18H10T; the results are presented. The effect produced by the nanostructured modifying powders added to the weld pool on the quality of weld joints was examined. The weld joints were obtained by arc welding in argon atmosphere using consumable electrode. Due to the weld pool modification, the dendrite size was found to decrease and a more equilibrium microstructure would form in the weld material. Режим доступа: по договору с организацией-держателем ресурса |
| Jazyk: | angličtina |
| Vydáno: |
2015
|
| Témata: | |
| On-line přístup: | http://dx.doi.org/10.1063/1.4932900 |
| Médium: | Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=645014 |
| Shrnutí: | Title screen The experimental studies were carried on for the test samples of welds of the steel 12X18H10T; the results are presented. The effect produced by the nanostructured modifying powders added to the weld pool on the quality of weld joints was examined. The weld joints were obtained by arc welding in argon atmosphere using consumable electrode. Due to the weld pool modification, the dendrite size was found to decrease and a more equilibrium microstructure would form in the weld material. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1063/1.4932900 |