The Tribological Properties and the Microstructure of Cu-Mo-S Coatings; AIP Conference Proceedings; Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures
| Parent link: | AIP Conference Proceedings Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures.— 2015.— [020203, 4 p.] |
|---|---|
| Korporativní autor: | |
| Další autoři: | , , , |
| Shrnutí: | Title screen Coatings on the basis of the Cu-Mo-S system were deposited on the Cu substrate by the method of pulse magnetron sputtering of a special composite target. The wear resistance of the coatings with a copper friction pair was studied using the tribological tests in argon and the air environment. The coating properties were investigated using a variety of methods including SEM, TEM/EDS, and XRD. The fiber-globular structure of the coatings was evaluated. The investigation showed that the Cu-Mo-S coatings could decrease the wear rate of a copper friction pair in ~350 times in the argon atmosphere. A decrease of the friction coefficient of the copper friction pair from 0.59 to 0.27 (with a coating) was observed during the tribological tests in the air environment. Режим доступа: по договору с организацией-держателем ресурса |
| Jazyk: | angličtina |
| Vydáno: |
2015
|
| Témata: | |
| On-line přístup: | http://dx.doi.org/10.1063/1.4932893 |
| Médium: | Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=645009 |