Investigation of the Serpentine Coating on the Steel Surface; AIP Conference Proceedings; Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures
| Parent link: | AIP Conference Proceedings Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures.— 2015.— [020099, 4 p.] |
|---|---|
| مؤلف مشترك: | |
| مؤلفون آخرون: | , , , , , |
| الملخص: | Title screen The structure and phase composition of geomodifiers coating obtained on the surface of steel balls are examined using optical metallography, SEM and XRD. Coating has been formed for 672 hours by mixing of serpentine powder with steel balls in a ball mill. The coating has an adhesive bond to the substrate. The phase composition of the coating is different from the phase composition of the initial powder. The formation of the magnesium silicate is caused by the process of dehydration. Dehydration occurs due to local temperature fluctuations in the contact areas of the steel framework and serpentine in their interaction. It was determined that for formation of the coating of certain phase composition cumulative release of heat must meet the heating temperature higher than 550°С. Режим доступа: по договору с организацией-держателем ресурса |
| اللغة: | الإنجليزية |
| منشور في: |
2015
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://dx.doi.org/10.1063/1.4932789 |
| التنسيق: | الكتروني فصل الكتاب |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=644942 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 644942 | ||
| 005 | 20240221111217.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\10026 | ||
| 035 | |a RU\TPU\network\10023 | ||
| 090 | |a 644942 | ||
| 100 | |a 20151204a2015 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Investigation of the Serpentine Coating on the Steel Surface |f Zh. G. Kovalevskaya [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 7 tit.] | ||
| 330 | |a The structure and phase composition of geomodifiers coating obtained on the surface of steel balls are examined using optical metallography, SEM and XRD. Coating has been formed for 672 hours by mixing of serpentine powder with steel balls in a ball mill. The coating has an adhesive bond to the substrate. The phase composition of the coating is different from the phase composition of the initial powder. The formation of the magnesium silicate is caused by the process of dehydration. Dehydration occurs due to local temperature fluctuations in the contact areas of the steel framework and serpentine in their interaction. It was determined that for formation of the coating of certain phase composition cumulative release of heat must meet the heating temperature higher than 550°С. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\4816 |t AIP Conference Proceedings | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\9779 |t Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures |o Proceedings of the International Conference, 21–25 September 2015, Tomsk, Russia |f National Research Tomsk Polytechnic University (TPU) ; ed. V. E. Panin ; S. G. Psakhie ; V. M. Fomin |v [020099, 4 p.] |d 2015 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a покрытия | |
| 610 | 1 | |a стальные поверхности | |
| 610 | 1 | |a фазовый состав | |
| 610 | 1 | |a структура | |
| 610 | 1 | |a оптическая металлография | |
| 610 | 1 | |a порошки | |
| 610 | 1 | |a дегидратация | |
| 701 | 1 | |a Kovalevskaya |b Zh. G. |c specialist in materials science |c Professor of Tomsk Polytechnic University, Doctor of Technical Sciences |f 1967- |g Zhanna Gennadievna |3 (RuTPU)RU\TPU\pers\32481 |9 16428 | |
| 701 | 1 | |a Khimich |b M. A. | |
| 701 | 1 | |a Veselov |b S. V. | |
| 701 | 1 | |a Belavskaya |b O. A. | |
| 701 | 1 | |a Tolmachev |b A. I. | |
| 701 | 1 | |a Bataev |b V. A. | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра материаловедения и технологии металлов (МТМ) |3 (RuTPU)RU\TPU\col\18689 |
| 801 | 2 | |a RU |b 63413507 |c 20151204 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1063/1.4932789 | |
| 942 | |c CF | ||