The Structure and Properties of Composites Al[2]O[3]-ZrO[2]-TiC for Use in Extreme Conditions; AIP Conference Proceedings; Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures

The Structure and Properties of Composites Al[2]O[3]-ZrO[2]-TiC for Use in Extreme Conditions

מידע ביבליוגרפי
Parent link:AIP Conference Proceedings
Vol. 1683 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures.— 2015.— [020061, 5 p.]
Corporate Authors: Национальный исследовательский Томский политехнический университет (ТПУ) Институт физики высоких технологий (ИФВТ) Кафедра материаловедения и технологии металлов (МТМ), Национальный исследовательский Томский политехнический университет (ТПУ) Институт физики высоких технологий (ИФВТ) Кафедра материаловедения в машиностроении (ММС)
מחברים אחרים: Grigoriev M. G. Mikhail Georgievich, Kotelnikov N. L., Buyakova S. P. Svetlana Petrovna, Kulkov S. N. Sergey Nikolaevich
סיכום:Title screen
The effect of adding nanocrystalline ZrO[2] and submicron TiC to ultrafine Al[2]O[3] on mechanical properties and the microstructure of the composites developed by hot pressing was investigated. It was shown that by means of hot pressing in an argon atmosphere at a sintering temperature of 1500 degrees one can obtain the composites Al[2]O[3]-ZrO[2]-TiC with a fine structure and minimal porosity. It has been shown that in material a multi-scale hierarchical structure is formed, which possesses high physical and mechanical properties: the hardness and fracture toughness was 21.5 GPa and 5.2 MPa×m{1/2} respectively, the modulus of elasticity was 500 GPa and bending strength was 390 MPa. Tests on composites' cutting properties were carried out on interrupted cutting of hardened steel. All samples had wear of the cutting edge in the form of chips of the grain rear working surface of the tool, but the cutting tool which was made by Al[2]O[3]-10% ZrO[2]-10% TiC had a minimum width of wear.
Режим доступа: по договору с организацией-держателем ресурса
שפה:אנגלית
יצא לאור: 2015
נושאים:
электронный ресурс
труды учёных ТПУ
структура
свойства
композиты
горячее прессование
нанокомпозиты
оксид алюминия
диоксид циркония
גישה מקוונת:http://dx.doi.org/10.1063/1.4932751
פורמט: אלקטרוני Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=644901

פריטים דומים

פריטים דומים