Plasma dynamic synthesis of ultradispersed copper oxides; IOP Conference Series: Materials Science and Engineering; Vol. 93: Modern Technique and Technologies (MTT'2015)
| Parent link: | IOP Conference Series: Materials Science and Engineering.— , 2009- Vol. 93: Modern Technique and Technologies (MTT'2015).— 2015.— [012019, 6 p.] |
|---|---|
| Ente Autore: | |
| Altri autori: | , , , |
| Riassunto: | Title screen Copper oxide is necessary material for production of superconductors. The issue of obtaining high purity and nanosides CuO is actual. This article shows the results on the obtaining of nanodispersed copper oxide by plasma dynamic method in system based on coaxial magneto plasma accelerator with copper electrodes. Such analyses of ultradispersed synthesized products as X-Ray diffractometry, IR-spectroscopy and thermal analysis were carried out. According to XRD such phases as copper Cu, copper oxide (I) Cu[2]O, copper oxide (II) CuO, and copper hydroxide hydrate Cu(OH)[2]xH[2]O were identified in the product. It was found that with the gradual heating of the initial product up to 800°С the phase content changed dramatically in terms of enhancing copper oxide phase (up to 97%). Режим доступа: по договору с организацией-держателем ресурса |
| Lingua: | inglese |
| Pubblicazione: |
2015
|
| Serie: | Power industry |
| Soggetti: | |
| Accesso online: | http://dx.doi.org/10.1088/1757-899X/93/1/012019 http://earchive.tpu.ru/handle/11683/19989 |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=644521 |
| Riassunto: | Title screen Copper oxide is necessary material for production of superconductors. The issue of obtaining high purity and nanosides CuO is actual. This article shows the results on the obtaining of nanodispersed copper oxide by plasma dynamic method in system based on coaxial magneto plasma accelerator with copper electrodes. Such analyses of ultradispersed synthesized products as X-Ray diffractometry, IR-spectroscopy and thermal analysis were carried out. According to XRD such phases as copper Cu, copper oxide (I) Cu[2]O, copper oxide (II) CuO, and copper hydroxide hydrate Cu(OH)[2]xH[2]O were identified in the product. It was found that with the gradual heating of the initial product up to 800°С the phase content changed dramatically in terms of enhancing copper oxide phase (up to 97%). Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1088/1757-899X/93/1/012019 |