Physics and chemistry of producing silicon-hydroxylapatite-titanium composite materials; IOP Conference Series: Materials Science and Engineering; Vol. 81 : Radiation-Thermal Effects and Processes in Inorganic Materials
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 81 : Radiation-Thermal Effects and Processes in Inorganic Materials.— 2015.— [012066, 8 p.] |
|---|---|
| Autori kompanije: | , |
| Daljnji autori: | , , , |
| Sažetak: | Title screen In the research, Si-HA poweders have been synthesized using SBF solution with different content of silicon. It was found that all the samples synthesized from the model solution of extracellular fluid under varying concentration of silicate ions are single-phase and repesent hydroxyapatite. The nature of the reagent containing SiO[44]- ions does not affect the hydroxyapatite structure. In the study of the surface and morphological characteristics of the phosphate coatings modified by silicon ions, it was found that as the degree of phosphate calcium substitution by SiO[44]- ions increases, the surface wettability on the titanium substrates deteriorates and cohesive energy decreases. It is shown that the titanium coating is formed in three stages. After irradiation of titanium substrates coated with Si-HA, the crystals can keep growing and the surface can keep regenerating. Режим доступа: по договору с организацией-держателем ресурса |
| Jezik: | engleski |
| Izdano: |
2015
|
| Teme: | |
| Online pristup: | http://dx.doi.org/10.1088/1757-899X/81/1/012066 http://earchive.tpu.ru/handle/11683/14712 |
| Format: | Elektronički Poglavlje knjige |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=642977 |
| Sažetak: | Title screen In the research, Si-HA poweders have been synthesized using SBF solution with different content of silicon. It was found that all the samples synthesized from the model solution of extracellular fluid under varying concentration of silicate ions are single-phase and repesent hydroxyapatite. The nature of the reagent containing SiO[44]- ions does not affect the hydroxyapatite structure. In the study of the surface and morphological characteristics of the phosphate coatings modified by silicon ions, it was found that as the degree of phosphate calcium substitution by SiO[44]- ions increases, the surface wettability on the titanium substrates deteriorates and cohesive energy decreases. It is shown that the titanium coating is formed in three stages. After irradiation of titanium substrates coated with Si-HA, the crystals can keep growing and the surface can keep regenerating. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| Digitalni identifikator objekta: | 10.1088/1757-899X/81/1/012066 |