Investigation of the morphology and elemental composition of the silicon-containing calcium phosphate coating treated by intensive pulsed electron beam; The 9th International Forum on Strategic Techology (IFOST-2014), September 21-23, 2014, Cox's Bazar, Bangladesh

Bibliographic Details
Parent link:	The 9th International Forum on Strategic Techology (IFOST-2014), September 21-23, 2014, Cox's Bazar, Bangladesh.— 2014.— [3 p.]
Corporate Authors:	Национальный исследовательский Томский политехнический университет (ТПУ) Институт кибернетики (ИК) Кафедра иностранных языков института кибернетики (ИЯИК), Национальный исследовательский Томский политехнический университет (ТПУ) Физико-технический институт (ФТИ) Кафедра теоретической и экспериментальной физики (ТиЭФ) Центр технологий (ЦТ), Национальный исследовательский Томский политехнический университет (ТПУ) Физико-технический институт (ФТИ) Кафедра теоретической и экспериментальной физики (ТиЭФ), Национальный исследовательский Томский политехнический университет (ТПУ) Физико-технический институт (ФТИ) Кафедра общей физики (ОФ), Национальный исследовательский Томский политехнический университет (ТПУ) Институт физики высоких технологий (ИФВТ) Кафедра сильноточной электроники (СЭ)
Other Authors:	Chudinova A. I. Alena Igorevna, Surmeneva (Ryabtseva) M. A. Maria Alexandrovna, Grubova I. Yu. Irina Yurievna, Pryamushko T. S. Tatiana Sergeevna, Pushilina N. S. Natalia Sergeevna, Teresov A. D., Koval N. N. Nikolay Nikolaevich, Prymak O., Epple M., Surmenev R. A. Roman Anatolievich
Summary:	Title screen The surface of titanium substrate with calcium phosphate (CaP) coating prepared by RF magnetron sputtering was treated by a pulsed electron beam with an energy density of 0.8 - 8 J/cm{2}. A partial or complete intermixing of the surface layers of the system CaP-titanium was observed. Significant changes in the topography of the formed surfaces were revealed. Treatment conditions with an energy density of 0.8 and 3 J/cm{2} led to the thermal annealing of the coating. The use of beam parameters with an energy density of 6.5 and 8 J/cm{2} led to the partial vaporization and intermixing of the coating with a titanium matrix.
Language:	English
Published:	2014
Series:	Civil Engineering, Urban Planning & Architecture Poster
Subjects:	электронный ресурс труды учёных ТПУ лечение электронные пучки фосфат кальция распыление