Structure of Sintered Ti–TiC Materials; Applied Mechanics and Materials; Vol. 682 : Innovation Technology and Economics in Engineering
| Parent link: | Applied Mechanics and Materials: Scientific Journal Vol. 682 : Innovation Technology and Economics in Engineering.— 2014.— [P. 127-131] |
|---|---|
| Huvudupphovsman: | |
| Institutionell upphovsman: | |
| Övriga upphovsmän: | , |
| Sammanfattning: | Title screen The results of studying of sintered powder Ti-TiC compositions are presented in this paper. Materials varying with carbon content and titanium powder dispersity sintered at 1300°С and were investigated. Sintering duration, carbon content and titanium dispersity were shown to influence on microstructure, average grain size, as well as porosity and crystal lattice parameters of titanium and titanium carbide. Режим доступа: по договору с организацией-держателем ресурса |
| Språk: | engelska |
| Publicerad: |
2014
|
| Serie: | Material Science, Machining Technologies and Equipments in Mechanical Engineering |
| Ämnen: | |
| Länkar: | http://dx.doi.org/10.4028/www.scientific.net/AMM.682.127 |
| Materialtyp: | Elektronisk Bokavsnitt |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=641452 |
| Sammanfattning: | Title screen The results of studying of sintered powder Ti-TiC compositions are presented in this paper. Materials varying with carbon content and titanium powder dispersity sintered at 1300°С and were investigated. Sintering duration, carbon content and titanium dispersity were shown to influence on microstructure, average grain size, as well as porosity and crystal lattice parameters of titanium and titanium carbide. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.4028/www.scientific.net/AMM.682.127 |