Plasmodynamic Synthesis of Nanodispersed Silicon Carbide
| Parent link: | Advanced Materials Research: Scientific Journal.— , 1994- Vol. 1040 : High Technology: Research and Applications 2014 (HTRA 2014).— 2014.— [P. 735-739] |
|---|---|
| Körperschaft: | |
| Weitere Verfasser: | , , , |
| Zusammenfassung: | Title screen The plasmodynamic synthesis was conducted in the electric hypervelocity pulse jet of carbon-silicon electric discharge plasma influenced on a copper target in an argon atmosphere. Some samples of a powder product with a high content of [betaъ-SiC were produced. The results of the experiments made at different levels of supplied energy were compared. It was shown that the sizes of crystals grew, when the energy of a plasma shot increased. Режим доступа: по договору с организацией-держателем ресурса |
| Veröffentlicht: |
2014
|
| Schriftenreihe: | Technologies of Electrophysical Methods of Materials Treatment |
| Schlagworte: | |
| Online-Zugang: | http://dx.doi.org/10.4028/www.scientific.net/AMR.1040.735 |
| Format: | Elektronisch Buchkapitel |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=641107 |
| Zusammenfassung: | Title screen The plasmodynamic synthesis was conducted in the electric hypervelocity pulse jet of carbon-silicon electric discharge plasma influenced on a copper target in an argon atmosphere. Some samples of a powder product with a high content of [betaъ-SiC were produced. The results of the experiments made at different levels of supplied energy were compared. It was shown that the sizes of crystals grew, when the energy of a plasma shot increased. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.4028/www.scientific.net/AMR.1040.735 |