Positron spectroscopy of defects in submicrocrystalline nickel after low-temperature annealing
| Parent link: | Physics of the Solid State: Scientific Journal Vol. 57, iss. 2.— 2015.— [P. 219-228] |
|---|---|
| Համատեղ հեղինակ: | |
| Այլ հեղինակներ: | , , , , , , |
| Ամփոփում: | Title screen Using the method of measuring the positron lifetime spectra and Doppler broadening annihilation line spectroscopy, the annealing of defects in submicrocrystalline nickel produced by equal channel angular pressing has been studied. In as-prepared samples, the positrons are trapped by dislocation defects and vacancy complexes inside crystallites. The size of vacancy complexes decreases with increasing annealing temperature in the interval deltaT = 20–300°C. However, at T = 360°C, the complexes start growing again. The dependence of S-parameter on W-parameter derived from the Doppler broadening spectroscopy has two parts with different inclinations to axes that correspond to different types of primary centers of positron trapping in submicrocrystalline nickel. It has been elucidated that, at recovery stage in the temperature interval deltaT = 20–180°C, the main centers of positron trapping are low-angle boundaries enriched by impurities, while at in situ recrystallization stage in the temperature interval deltaT = 180–360°C, the primary centers of positron trapping are low-angle boundaries. Режим доступа: по договору с организацией-держателем ресурса |
| Լեզու: | անգլերեն |
| Հրապարակվել է: |
2015
|
| Խորագրեր: | |
| Առցանց հասանելիություն: | http://dx.doi.org/10.1134/S1063783415020225 |
| Ձևաչափ: | Էլեկտրոնային Գրքի գլուխ |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=641047 |
| Ամփոփում: | Title screen Using the method of measuring the positron lifetime spectra and Doppler broadening annihilation line spectroscopy, the annealing of defects in submicrocrystalline nickel produced by equal channel angular pressing has been studied. In as-prepared samples, the positrons are trapped by dislocation defects and vacancy complexes inside crystallites. The size of vacancy complexes decreases with increasing annealing temperature in the interval deltaT = 20–300°C. However, at T = 360°C, the complexes start growing again. The dependence of S-parameter on W-parameter derived from the Doppler broadening spectroscopy has two parts with different inclinations to axes that correspond to different types of primary centers of positron trapping in submicrocrystalline nickel. It has been elucidated that, at recovery stage in the temperature interval deltaT = 20–180°C, the main centers of positron trapping are low-angle boundaries enriched by impurities, while at in situ recrystallization stage in the temperature interval deltaT = 180–360°C, the primary centers of positron trapping are low-angle boundaries. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1134/S1063783415020225 |