Changes in the Spectral Characteristics of Aluminum Films Deposited under Assisting Argon Ion Beam
| Источник: | Advanced Materials Research : Radiation and nuclear techniques in material science: Scientific Journal Vol. 1084 : Physical-Technical Problems of Nuclear Science, Energy Generation, and Power Industry (PTPAI -2014).— 2015.— [P. 11-15] |
|---|---|
| Автор-организация: | |
| Другие авторы: | , , , |
| Примечания: | Title screen High-reflectance aluminum films are widely used in applied optics. As part of this work, we deposited aluminum films on glass substrates by magnetron sputtering using argon ion beam assistance. The reflectivity of the films obtained was measured on the SF-256 spectrophotometer. The microstructure and topology of the films were examined with a transmission electron microscope (TEM), X-ray diffraction (XRD) and atomic force microscope (AFM). The studies have shown that the aluminum films deposited with ion assistance have higher reflectance in the UV range than the films formed by magnetron sputtering alone. The results of TEM and AFM measurements show that the geometric factor (crystallite size, surface roughness) is not the reason for the increase of reflectivity. X-ray diffraction analyses have shown a significant increase in microstress in the aluminum films deposited with ion assistance, which is caused by an increase in the defect density of the vacancy-type crystal structure. The results have shown that the increase in the density of crystal defects leads to an increase in reflectance in the UV range. Режим доступа: по договору с организацией-держателем ресурса |
| Язык: | английский |
| Опубликовано: |
2015
|
| Серии: | Materials Science and Technologies |
| Предметы: | |
| Online-ссылка: | http://dx.doi.org/10.4028/www.scientific.net/AMR.1084.11 |
| Формат: | Электронный ресурс Статья |
| Запись в KOHA: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=640188 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 640188 | ||
| 005 | 20250512142800.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\4734 | ||
| 035 | |a RU\TPU\network\4732 | ||
| 090 | |a 640188 | ||
| 100 | |a 20150413a2015 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Changes in the Spectral Characteristics of Aluminum Films Deposited under Assisting Argon Ion Beam |f S. P. Umnov [et al.] | |
| 203 | |a Text |c electronic | ||
| 225 | 1 | |a Materials Science and Technologies | |
| 300 | |a Title screen | ||
| 330 | |a High-reflectance aluminum films are widely used in applied optics. As part of this work, we deposited aluminum films on glass substrates by magnetron sputtering using argon ion beam assistance. The reflectivity of the films obtained was measured on the SF-256 spectrophotometer. The microstructure and topology of the films were examined with a transmission electron microscope (TEM), X-ray diffraction (XRD) and atomic force microscope (AFM). The studies have shown that the aluminum films deposited with ion assistance have higher reflectance in the UV range than the films formed by magnetron sputtering alone. The results of TEM and AFM measurements show that the geometric factor (crystallite size, surface roughness) is not the reason for the increase of reflectivity. X-ray diffraction analyses have shown a significant increase in microstress in the aluminum films deposited with ion assistance, which is caused by an increase in the defect density of the vacancy-type crystal structure. The results have shown that the increase in the density of crystal defects leads to an increase in reflectance in the UV range. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\network\4598 |t Advanced Materials Research : Radiation and nuclear techniques in material science |o Scientific Journal | |
| 463 | 1 | |0 (RuTPU)RU\TPU\network\4600 |t Vol. 1084 : Physical-Technical Problems of Nuclear Science, Energy Generation, and Power Industry (PTPAI -2014) |o The VIth International Conference, June 5-7, 2014, Tomsk, Russia |o [proceedings] |f National Research Tomsk Polytechnic University (TPU) |v [P. 11-15] |d 2015 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a спектральные характеристики | |
| 610 | 1 | |a алюминиевые пленки | |
| 610 | 1 | |a пучки | |
| 610 | 1 | |a ионы | |
| 610 | 1 | |a аргон | |
| 610 | 1 | |a магнетронное распыление | |
| 610 | 1 | |a коэффициент | |
| 610 | 1 | |a распыление | |
| 610 | 1 | |a рентгеновские лучи | |
| 610 | 1 | |a алюминиевые пленки | |
| 610 | 1 | |a кристаллические решетки | |
| 701 | 1 | |a Umnov |b S. P. |c physicist |c Senior researcher of Tomsk Polytechnic University, Candidate of physical and mathematical sciences |f 1957- |g Sergey Pavlovich |3 (RuTPU)RU\TPU\pers\34215 | |
| 701 | 1 | |a Asainov |b O. Kh. |c physicist |c Head of the laboratory of Tomsk Polytechnic University, Candidate of physical and mathematical sciences |f 1957- |g Oleg Khaydarovich |3 (RuTPU)RU\TPU\pers\34632 | |
| 701 | 1 | |a Popova |b S. N. | |
| 701 | 1 | |a Lemachko |b A. N. | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |c (2009- ) |9 26305 |
| 801 | 2 | |a RU |b 63413507 |c 20161228 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u http://dx.doi.org/10.4028/www.scientific.net/AMR.1084.11 | |
| 942 | |c CF | ||