Friction stir processing on carbon steel; AIP Conference Proceedings; Vol. 1623 : International Conference on Physical Mesomechanics of Multilevel Systems 2014, Tomsk, Russia, 3–5 September 2014
| Parent link: | AIP Conference Proceedings Vol. 1623 : International Conference on Physical Mesomechanics of Multilevel Systems 2014, Tomsk, Russia, 3–5 September 2014.— 2014.— [P. 627-630] |
|---|---|
| Prif Awdur: | |
| Awduron Corfforaethol: | , |
| Awduron Eraill: | , |
| Crynodeb: | Title screen Friction stir processing of medium carbon steel samples has been carried out using a milling machine and toolsmade of cemented tungsten carbide. Samples have been machined from 40 and 40X steels. The tools have been made inthe shape of 5u5u1.5 mm and 3u3u1.5 mm tetrahedrons. The microstructure of stirred zone has been obtained using thesmaller tool and consists of fine recrystallized 2–3 Pm grains, whereas the larger tool has produced the “onion-like”structures comprising hard quenched “white” 500–600 MPa layers with 300–350 MPa interlayers of bainite needles. Themean values of wear intensity obtained after measuring the wear scar width were 0.02 mm/m and 0.001 mm/m for nonprocessedand processed samples, respectively. Режим доступа: по договору с организацией-держателем ресурса |
| Iaith: | Saesneg |
| Cyhoeddwyd: |
2014
|
| Pynciau: | |
| Mynediad Ar-lein: | http://dx.doi.org/10.1063/1.4899023 http://earchive.tpu.ru/handle/11683/35693 |
| Fformat: | Electronig Pennod Llyfr |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=639997 |