Investigation of the Properties of Alumina-Zirconia Ceramics
| Parent link: | Advanced Materials Research: Scientific Journal Vol. 1040 : High Technology: Research and Applications 2014 (HTRA 2014).— 2014.— [P. 245-249] |
|---|---|
| Հիմնական հեղինակ: | |
| Համատեղ հեղինակ: | |
| Այլ հեղինակներ: | , , |
| Ամփոփում: | Title screen The article focuses on the investigation of the properties of alumina-zirconia ceramics possessing high mechanical characteristics and good conductivity at high temperatures. Measurement results of the dielectric dissipation factor, dielectric constant, electric conductivity when using direct and alternating current for the ceramics samples of 80%(ZrO[2]-3%Y[2]O[3])-20% Al[2]O[3] composition are presented in the paper. Measurements were conducted simultaneously in the electrostatic field in vacuum while heating the samples to the temperatures ranging from 300 to 1700K. Investigations showed that alumina-zirconia ceramics at high temperatures obtains ferroelectric properties not typical of these structures. Режим доступа: по договору с организацией-держателем ресурса |
| Լեզու: | անգլերեն |
| Հրապարակվել է: |
2014
|
| Խորագրեր: | |
| Առցանց հասանելիություն: | http://dx.doi.org/10.4028/www.scientific.net/AMR.1040.245 |
| Ձևաչափ: | Էլեկտրոնային Գրքի գլուխ |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=638591 |
| Ամփոփում: | Title screen The article focuses on the investigation of the properties of alumina-zirconia ceramics possessing high mechanical characteristics and good conductivity at high temperatures. Measurement results of the dielectric dissipation factor, dielectric constant, electric conductivity when using direct and alternating current for the ceramics samples of 80%(ZrO[2]-3%Y[2]O[3])-20% Al[2]O[3] composition are presented in the paper. Measurements were conducted simultaneously in the electrostatic field in vacuum while heating the samples to the temperatures ranging from 300 to 1700K. Investigations showed that alumina-zirconia ceramics at high temperatures obtains ferroelectric properties not typical of these structures. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.4028/www.scientific.net/AMR.1040.245 |