Features of phase formation of mullite-corundum materials in mixtures of kaolin with a fluoriding component
| Parent link: | Refractories and Industrial Ceramics Vol. 51, iss. 3.— 2010.— [P. 197-201] |
|---|---|
| מחבר תאגידי: | |
| מחברים אחרים: | , , , |
| סיכום: | Title screen Processes are studied for synthesis of mullite from kaolin by an unusual method (by fluoride technology) in the temperature range from 850 to 1300°C. Depending on the amount of added fluorine agent it is possible to regulate the ratio of crystal phases that form (acicular mullite and lamellar corundum), that creates prerequisites for controlling preparation of aluminosilicate ceramic with a specific phase composition and a predictable microstructure Режим доступа: по договору с организацией-держателем ресурса |
| יצא לאור: |
2010
|
| נושאים: | |
| גישה מקוונת: | http://link.springer.com/article/10.1007%2Fs11148-010-9288-3?LI=true |
| פורמט: | אלקטרוני Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=637372 |
| סיכום: | Title screen Processes are studied for synthesis of mullite from kaolin by an unusual method (by fluoride technology) in the temperature range from 850 to 1300°C. Depending on the amount of added fluorine agent it is possible to regulate the ratio of crystal phases that form (acicular mullite and lamellar corundum), that creates prerequisites for controlling preparation of aluminosilicate ceramic with a specific phase composition and a predictable microstructure Режим доступа: по договору с организацией-держателем ресурса |
|---|