| Parent link: | Thermosense XXIX, Orlando, April 09-12, 2007: Proc. SPIE 6541. [12 p.].— , 2007 |
|---|---|
| Daljnji autori: | , , , |
| Sažetak: | Title screen The paper describes theoretical and experimental results of the inspection of 5 mm- and 15 mm-thick filament wound CFRP shell samples containing Teflon inserts as defect surrogates. Heating was accomplished with a 30 kW tubular quartz lamp heater which provided up to 14 kW/m2 of absorbed power. Thermal properties of the samples were evaluated including the analysis of diffusivity anisotropy. Both one- and two-sided test procedures were comparatively investigated to illustrate difficulties which appeared in the inspection of thick composites Режим доступа: по договору с организацией-держателем ресурса |
| Izdano: |
2007
|
| Teme: | |
| Online pristup: | http://proceedings.spiedigitallibrary.org/proceeding.aspx?articleid=1301850 |
| Format: | Elektronički Poglavlje knjige |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=636989 |
| Sažetak: | Title screen The paper describes theoretical and experimental results of the inspection of 5 mm- and 15 mm-thick filament wound CFRP shell samples containing Teflon inserts as defect surrogates. Heating was accomplished with a 30 kW tubular quartz lamp heater which provided up to 14 kW/m2 of absorbed power. Thermal properties of the samples were evaluated including the analysis of diffusivity anisotropy. Both one- and two-sided test procedures were comparatively investigated to illustrate difficulties which appeared in the inspection of thick composites Режим доступа: по договору с организацией-держателем ресурса |
|---|