Influence of the modification process on the properties of AlOOH nanofibers; Russian Journal of Applied Chemistry; Vol. 86, iss. 3
| Parent link: | Russian Journal of Applied Chemistry: Scientific Journal Vol. 86, iss. 3.— 2013.— [P. 360-365] |
|---|---|
| Beste egile batzuk: | , , , |
| Gaia: | Title screen A procedure of bulk modification of aluminum oxhydroxide AlOOH during synthesis using manganese(II) ion as the modifying agent was studied. The physicochemical properties of the modified AlOOH fiber were examined. It was found that the presence of manganese(II) ions in solution affected the composition of the products of the reaction between aluminum nanopowder and “liquid water.” The phase composition of the reaction products was examined by X-ray diffraction and differential thermal analysis techniques. It was shown that, for solutions with the manganese ion concentration varying from 0.02 x 10-3 to 40 x 10-3 mol l-1, the degree of amorphicity and the proportion of the AlOOH phase tended to increase. A modification mechanism involving the participation of manganese ions in the AlOOH nanofiber growth process was proposed Режим доступа: по договору с организацией-держателем ресурса |
| Hizkuntza: | ingelesa |
| Argitaratua: |
2013
|
| Gaiak: | |
| Sarrera elektronikoa: | http://dx.doi.org/10.1134/S1070427213030129 |
| Formatua: | Baliabide elektronikoa Liburu kapitulua |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=636693 |
MARC
| LEADER | 00000nla0a2200000 4500 | ||
|---|---|---|---|
| 001 | 636693 | ||
| 005 | 20250403084652.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\734 | ||
| 090 | |a 636693 | ||
| 100 | |a 20140304d2013 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drnn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Influence of the modification process on the properties of AlOOH nanofibers |f E. N. Gryaznova [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 365 (16 tit.)] | ||
| 330 | |a A procedure of bulk modification of aluminum oxhydroxide AlOOH during synthesis using manganese(II) ion as the modifying agent was studied. The physicochemical properties of the modified AlOOH fiber were examined. It was found that the presence of manganese(II) ions in solution affected the composition of the products of the reaction between aluminum nanopowder and “liquid water.” The phase composition of the reaction products was examined by X-ray diffraction and differential thermal analysis techniques. It was shown that, for solutions with the manganese ion concentration varying from 0.02 x 10-3 to 40 x 10-3 mol l-1, the degree of amorphicity and the proportion of the AlOOH phase tended to increase. A modification mechanism involving the participation of manganese ions in the AlOOH nanofiber growth process was proposed | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Russian Journal of Applied Chemistry |o Scientific Journal | ||
| 463 | |t Vol. 86, iss. 3 |v [P. 360-365] |d 2013 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 701 | 1 | |a Gryaznova |b E. N. |c chemical engineer |c Engineer-researcher of Tomsk Polytechnic University |f 1987- |g Elena Nikolaevna |3 (RuTPU)RU\TPU\pers\31929 | |
| 701 | 1 | |a Shiyan |b L. N. |c chemist |c Associate Professor of Tomsk Polytechnic University, Candidate of physical and mathematical sciences |f 1952- |g Lyudmila Nikolaevna |3 (RuTPU)RU\TPU\pers\31523 | |
| 701 | 1 | |a Yavorovsky |b N. A. |c physicist |c Head of the laboratory of Tomsk Polytechnic University, Candidate of technical sciences |f 1941- |g Nikolay Aleksandrovich |3 (RuTPU)RU\TPU\pers\31935 | |
| 701 | 1 | |a Korobochkin |b V. V. |c Chemical Engineer |c Head of the Department of Tomsk Polytechnic University, Doctor of technical sciences |f 1951- |g Valery Vasilievich |3 (RuTPU)RU\TPU\pers\31050 | |
| 801 | 2 | |a RU |b 63413507 |c 20160216 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1134/S1070427213030129 | |
| 942 | |c CF | ||