Friction and the development of hard alloy surface microstructures during wear; Journal of Materials Engineering and Performance; Vol. 6, iss. 6
| Parent link: | Journal of Materials Engineering and Performance: Scientific Journal Vol. 6, iss. 6.— 1997.— [P. 737-742] |
|---|---|
| 1. autor: | |
| Kolejni autorzy: | |
| Streszczenie: | Title screen Investigations of wear in sliding friction of WC-Hadfield steel hard alloy against cast tool steel have been carried out in a broad range of velocities and pressure values. Structural and phase composition variations have been revealed. Friction-affected zone was found to be 450 µm in depth. Structural a, transformation regions are located within 100 µm of the surface. These transformations contributed to the total solid solution deformation hardening Режим доступа: по договору с организацией-держателем ресурса |
| Język: | angielski |
| Wydane: |
1997
|
| Hasła przedmiotowe: | |
| Dostęp online: | http://dx.doi.org/10.1007/s11665-997-0075-3 |
| Format: | Elektroniczne Rozdział |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=636235 |
| Streszczenie: | Title screen Investigations of wear in sliding friction of WC-Hadfield steel hard alloy against cast tool steel have been carried out in a broad range of velocities and pressure values. Structural and phase composition variations have been revealed. Friction-affected zone was found to be 450 µm in depth. Structural a, transformation regions are located within 100 µm of the surface. These transformations contributed to the total solid solution deformation hardening Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1007/s11665-997-0075-3 |