Structure and abrasive wear resistance of R6M5 steel-tungsten carbide composite coatings; Technical Physics Letters; Vol. 38, iss. 9
| Parent link: | Technical Physics Letters: Scientific Journal Vol. 38, iss. 9.— 2012.— [P. 861-864] |
|---|---|
| Autor Principal: | |
| Autor Corporativo: | |
| Summary: | Title screen Features of the structure formation, composition, and abrasive wear resistance of R6M5 steel-tungsten carbide (R6M5-WC) composite coatings have been studied as dependent on the WC content. The introduction of 20 wt % WC into the hardening composition leads to an increase in the fraction of M6C carbide (in the form of eutectic inclusions with average size 5.9 ?m at grain boundaries and dispersed 0.25 m particles in the volume of grains), while a large proportion of metastable austenite (88 vol %) is still retained. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | inglés |
| Publicado: |
2012
|
| Subjects: | |
| Acceso en liña: | http://dx.doi.org/10.1134/S1063785012090210 |
| Formato: | MixedMaterials Electrónico Capítulo de libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=636197 |
MARC
| LEADER | 00000nla0a2200000 4500 | ||
|---|---|---|---|
| 001 | 636197 | ||
| 005 | 20250318135350.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\79 | ||
| 035 | |a RU\TPU\network\70 | ||
| 090 | |a 636197 | ||
| 100 | |a 20131014d2012 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Structure and abrasive wear resistance of R6M5 steel-tungsten carbide composite coatings |f S. F. Gnyusov | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 864 (7 tit.)] | ||
| 330 | |a Features of the structure formation, composition, and abrasive wear resistance of R6M5 steel-tungsten carbide (R6M5-WC) composite coatings have been studied as dependent on the WC content. The introduction of 20 wt % WC into the hardening composition leads to an increase in the fraction of M6C carbide (in the form of eutectic inclusions with average size 5.9 ?m at grain boundaries and dispersed 0.25 m particles in the volume of grains), while a large proportion of metastable austenite (88 vol %) is still retained. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Technical Physics Letters |o Scientific Journal | ||
| 463 | |t Vol. 38, iss. 9 |v [P. 861-864] |d 2012 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a износостойкость | |
| 610 | 1 | |a композитные покрятия | |
| 700 | 1 | |a Gnyusov |b S. F. |c specialist in the field of mechanical engineering |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1960- |g Sergey Fedorovich |3 (RuTPU)RU\TPU\pers\31403 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра физики высоких технологий в машиностроении (ФВТМ) |3 (RuTPU)RU\TPU\col\18687 |
| 801 | 2 | |a RU |b 63413507 |c 20170620 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1134/S1063785012090210 | |
| 942 | |c CF | ||