Влияние водорода на структурно-фазовое состояние и механические свойства циркониевого сплава Zr-2.5Nb; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XIX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 26-29 апреля 2022 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2022 Т. 1 : Физика.— 2022.— [С. 107-109] |
|---|---|
| المؤلف الرئيسي: | |
| مؤلف مشترك: | |
| مؤلفون آخرون: | |
| الملخص: | Заглавие с экрана Hydride-forming alloys of the Zr-Nb-H system are analyzed. In the initial state in the Zr-2.5Nb alloy, particles of the Nbβ phase are observed in the bulk and at the grain boundaries. In addition to the main Zrα phase, the Nbβ phase appears in the Zr-2.5Nb-0.19Н alloy and precipitations of ZrН and ZrН2 hydrides are also observed. The microhardness of the Zr-2.5Nb alloy samples is (130±7) HV, and after hydrogenation this value rises by 1.3 times, up to (166±7) HV. The value of the yield strength for both samples is comparable within the error values. The value of the tensile strength for the hydrogenated sample is 4.3% higher than for the original sample. For a sample with 0.19 wt. % hydrogen, value of deformation to failure is 2.1% less compared to the original sample not containing hydrogen. |
| اللغة: | الروسية |
| منشور في: |
2022
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | http://earchive.tpu.ru/handle/11683/72912 |
| التنسيق: | الكتروني فصل الكتاب |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=634685 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 634685 | ||
| 005 | 20250522151110.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\36503 | ||
| 035 | |a RU\TPU\conf\36501 | ||
| 090 | |a 634685 | ||
| 100 | |a 20220817d2022 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние водорода на структурно-фазовое состояние и механические свойства циркониевого сплава Zr-2.5Nb |d Influence of hydrogen on the structural and phase state and mechanical properties of zirconium Zr-2.5Nb alloy |f М. А. Кругляков |g науч. рук. Е. Н. Степанова | |
| 203 | |a Текст |c электронный | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 109 (2 назв.)] | ||
| 330 | |a Hydride-forming alloys of the Zr-Nb-H system are analyzed. In the initial state in the Zr-2.5Nb alloy, particles of the Nbβ phase are observed in the bulk and at the grain boundaries. In addition to the main Zrα phase, the Nbβ phase appears in the Zr-2.5Nb-0.19Н alloy and precipitations of ZrН and ZrН2 hydrides are also observed. The microhardness of the Zr-2.5Nb alloy samples is (130±7) HV, and after hydrogenation this value rises by 1.3 times, up to (166±7) HV. The value of the yield strength for both samples is comparable within the error values. The value of the tensile strength for the hydrogenated sample is 4.3% higher than for the original sample. For a sample with 0.19 wt. % hydrogen, value of deformation to failure is 2.1% less compared to the original sample not containing hydrogen. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\36478 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XIX Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 26-29 апреля 2022 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2022 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\36479 |t Т. 1 : Физика |v [С. 107-109] |d 2022 | |
| 510 | 1 | |a Influence of hydrogen on the structural and phase state and mechanical properties of zirconium Zr-2.5Nb alloy |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a водород | |
| 610 | 1 | |a структурно-фазовое состояние | |
| 610 | 1 | |a механические свойства | |
| 610 | 1 | |a циркониевые сплавы | |
| 610 | 1 | |a гидридообразующие сплавы | |
| 610 | 1 | |a наводороживание | |
| 610 | 1 | |a микротвердость | |
| 610 | 1 | |a деформации | |
| 700 | 1 | |a Кругляков |b М. А. |c физик |c инженер Томского политехнического университета |f 1997- |g Марк Александрович |3 (RuTPU)RU\TPU\pers\47299 |9 22879 | |
| 702 | 1 | |a Степанова |b Е. Н. |c физик |c доцент Томского политехнического университета, кандидат технических наук |f 1981- |g Екатерина Николаевна |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Отделение экспериментальной физики |3 (RuTPU)RU\TPU\col\23549 |
| 801 | 2 | |a RU |b 63413507 |c 20220908 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/72912 | |
| 942 | |c CF | ||