Структурно-фазовый состав материала изделия из сплава ЖС6У, сформированного методом проволочной электронно-лучевой аддитивной технологии; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XVIII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 27-30 апреля 2021 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2021 Т. 1 : Физика.— 2021.— [С. 100-102] |
|---|---|
| Autor principal: | |
| Autor corporatiu: | |
| Altres autors: | , , |
| Sumari: | Заглавие с экрана In the present work, a product of ZhS6U alloy was obtained by wire-feed electron-beam additive technology on a substrate of austenitic steel. The obtained product had the shape of a thin wall and contained 20 layers and was 4.5 cm high, had no surface macro-defects and deviations from the specified geometry. The structure of the material was represented by dendrite colonies growing epitaxially in the direction of additive growth with deviation in the direction of the electron beam motion. It is shown that in the material of the additive product there is a tenfold refinement of the structure and the main strengthening phases, compared to the raw cast material. Also, studies have shown that the foreign substrate material has no crystallographic effect on the product being formed, and its submergence is already leveled at 5 mm. |
| Idioma: | rus |
| Publicat: |
2021
|
| Matèries: | |
| Accés en línia: | http://earchive.tpu.ru/handle/11683/68351 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=633392 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 633392 | ||
| 005 | 20231101133747.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\35140 | ||
| 035 | |a RU\TPU\conf\35073 | ||
| 090 | |a 633392 | ||
| 100 | |a 20210817d2021 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Структурно-фазовый состав материала изделия из сплава ЖС6У, сформированного методом проволочной электронно-лучевой аддитивной технологии |d Structural-phase material composition of ZHS6U alloy product formed by wire-feed electron beam additive manufacturing |f Д. А. Гурьянов, К. С. Осипович, А. В. Воронцов |g науч. рук. Е. А. Колубаев | |
| 203 | |a Текст |c электронный | ||
| 230 | |a 1 компьютерный файл (pdf; 188 Kb) | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 102 (3 назв.)] | ||
| 330 | |a In the present work, a product of ZhS6U alloy was obtained by wire-feed electron-beam additive technology on a substrate of austenitic steel. The obtained product had the shape of a thin wall and contained 20 layers and was 4.5 cm high, had no surface macro-defects and deviations from the specified geometry. The structure of the material was represented by dendrite colonies growing epitaxially in the direction of additive growth with deviation in the direction of the electron beam motion. It is shown that in the material of the additive product there is a tenfold refinement of the structure and the main strengthening phases, compared to the raw cast material. Also, studies have shown that the foreign substrate material has no crystallographic effect on the product being formed, and its submergence is already leveled at 5 mm. | ||
| 338 | |b Российский фонд фундаментальных исследований |d 20-32-90010 | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\35054 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XVIII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 27-30 апреля 2021 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2021 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\35055 |t Т. 1 : Физика |v [С. 100-102] |d 2021 | |
| 510 | 1 | |a Structural-phase material composition of ZHS6U alloy product formed by wire-feed electron beam additive manufacturing |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a фазовые составы | |
| 610 | 1 | |a сплавы | |
| 610 | 1 | |a аддитивные технологии | |
| 610 | 1 | |a аустенитные стали | |
| 610 | 1 | |a подложки | |
| 610 | 1 | |a структурные элементы | |
| 700 | 1 | |a Гурьянов |b Д. А. |c физик |c инженер Томского политехнического университета |f 1993- |g Денис Андреевич |2 stltpush |3 (RuTPU)RU\TPU\pers\46935 | |
| 701 | 1 | |a Осипович |b К. С. | |
| 701 | 1 | |a Воронцов |b А. В. | |
| 702 | 1 | |a Колубаев |b Е. А. |c физик |c инженер Томского политехнического университета, кандидат физико-математических наук |f 1979- |g Евгений Александрович |2 stltpush |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Отделение материаловедения |h 7871 |2 stltpush |3 (RuTPU)RU\TPU\col\23508 |
| 801 | 2 | |a RU |b 63413507 |c 20210902 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/68351 | |
| 942 | |c BK | ||