Формирование фазы Ti2Ni и ее взаимодействие с водородом
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XVIII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 27-30 апреля 2021 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2021 Т. 2 : Химия.— 2021.— [С. 14-16] |
|---|---|
| Prif Awdur: | |
| Awdur Corfforaethol: | |
| Awduron Eraill: | |
| Crynodeb: | Заглавие с экрана It has been studied a formation of the Ti2Ni phase at adding titanium to a powder mixture and its interaction with hydrogen. The average size of the powder particles measured by SEM decreases from 15,7 µm to 11,5 µm ( 15 % mass. Ti in initial powder mixture). Mechanical alloying and annealing of powders lead to the formation of biphasic region consists of Ti2Ni with a maximum relative content with the introduction of 16 % of the mass. titanium into the initial powder mixture. The CDD size of the Ti2Ni phase increase from 43 to 62 ± 10 nm with increase hydrogination time. |
| Iaith: | Rwseg |
| Cyhoeddwyd: |
2021
|
| Pynciau: | |
| Mynediad Ar-lein: | http://earchive.tpu.ru/handle/11683/68281 |
| Fformat: | Electronig Pennod Llyfr |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=633328 |
| Crynodeb: | Заглавие с экрана It has been studied a formation of the Ti2Ni phase at adding titanium to a powder mixture and its interaction with hydrogen. The average size of the powder particles measured by SEM decreases from 15,7 µm to 11,5 µm ( 15 % mass. Ti in initial powder mixture). Mechanical alloying and annealing of powders lead to the formation of biphasic region consists of Ti2Ni with a maximum relative content with the introduction of 16 % of the mass. titanium into the initial powder mixture. The CDD size of the Ti2Ni phase increase from 43 to 62 ± 10 nm with increase hydrogination time. |
|---|