Влияние содержания карбида кремния на уплотнение композитов TiB2-SiC; Научная инициатива иностранных студентов и аспирантов; Т. 1
| Parent link: | Научная инициатива иностранных студентов и аспирантов: сборник докладовI Международной научно-практической конференции, Томск, 27-29 апреля 2021 г./ Национальный исследовательский Томский политехнический университет, Школа базовой инженерной подготовки.— , 2021 Т. 1.— 2021.— [С. 331-333] |
|---|---|
| Yazar: | |
| Müşterek Yazar: | |
| Diğer Yazarlar: | , |
| Özet: | Заглавие с титульного экрана The aim of this study was to investigate the effect of SiC additives on the sinterability and microstructure of TiB2-based ceramics. The samples were fabricated by hot pressing method at 1800 ℃. Due to the use of hot pressing, all samples reached a relative density of more than 90%. As far as TiB2-SiC composites are concerned, no formation of new substances was found in the reaction. On the other hand, X-ray diffraction (XRD) patterns as well as microstructural observations showed that the reflection intensity of silicon carbide was lower when showing X-ray diffraction patterns of samples with SiC content up to 10 vol. %. In addition, the elastic modulus and microhardness of the TiB2-SiC substances were elevated with the increase of SiC content. |
| Dil: | Rusça |
| Baskı/Yayın Bilgisi: |
2021
|
| Seri Bilgileri: | Актуальные проблемы инженерных наук |
| Konular: | |
| Online Erişim: | http://earchive.tpu.ru/handle/11683/67795 |
| Materyal Türü: | Elektronik Kitap Bölümü |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=633067 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 633067 | ||
| 005 | 20231101133737.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\34800 | ||
| 035 | |a RU\TPU\conf\34792 | ||
| 090 | |a 633067 | ||
| 100 | |a 20210624d2021 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 101zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние содержания карбида кремния на уплотнение композитов TiB2-SiC |f Ян Сяо, А. Г. Бурлаченко |g науч. рук. С. П. Буякова | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Актуальные проблемы инженерных наук | |
| 230 | |a 1 компьютерный файл (pdf; 660 Kb) | ||
| 300 | |a Заглавие с титульного экрана | ||
| 330 | |a The aim of this study was to investigate the effect of SiC additives on the sinterability and microstructure of TiB2-based ceramics. The samples were fabricated by hot pressing method at 1800 ℃. Due to the use of hot pressing, all samples reached a relative density of more than 90%. As far as TiB2-SiC composites are concerned, no formation of new substances was found in the reaction. On the other hand, X-ray diffraction (XRD) patterns as well as microstructural observations showed that the reflection intensity of silicon carbide was lower when showing X-ray diffraction patterns of samples with SiC content up to 10 vol. %. In addition, the elastic modulus and microhardness of the TiB2-SiC substances were elevated with the increase of SiC content. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\34751 |t Научная инициатива иностранных студентов и аспирантов |o сборник докладовI Международной научно-практической конференции, Томск, 27-29 апреля 2021 г. |o в 2 т. |f Национальный исследовательский Томский политехнический университет, Школа базовой инженерной подготовки |d 2021 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\34753 |t Т. 1 |v [С. 331-333] |d 2021 | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a карбид кремния | |
| 610 | 1 | |a уплотнения | |
| 610 | 1 | |a композиты | |
| 610 | 1 | |a диборид титана | |
| 610 | 1 | |a спекание | |
| 610 | 1 | |a пористость | |
| 700 | 0 | |a Ян Сяо | |
| 701 | 1 | |a Бурлаченко |b А. Г. |g Александр Геннадьевич | |
| 702 | 1 | |a Буякова |b С. П. |c специалист в области материаловедения |c профессор Томского политехнического университета, доктор технических наук |f 1968- |g Светлана Петровна |2 stltpush |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Отделение материаловедения |h 7871 |2 stltpush |3 (RuTPU)RU\TPU\col\23508 |
| 801 | 2 | |a RU |b 63413507 |c 20210625 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/67795 | |
| 942 | |c BK | ||