Структурно-фазовые превращения в высокоазотистой Cr-Mn-N стали при старении; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XVII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 21-24 апреля 2020 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2020 Т. 1 : Физика.— 2020.— [С. 209-211] |
|---|---|
| Hovedforfatter: | |
| Institution som forfatter: | |
| Andre forfattere: | , , |
| Summary: | Заглавие с экрана In the present work, the structure and phase composition of a high nitrogen austenitic steel were studied in dependence on the aging temperature from 600°C to 800°C. Age-hardening in the regimes 600°С, 5 h., 700°С, 0,5 h., и 800°С, 10 min. is accompanied with a decomposition of a [delta]-ferrite into a [sigma]-phase and an austenite, and simulteneous discontinuous decomposition of austenite with the formation of Cr[2]N-cells along grain boundaries and cells of austenite depleted by interstitials. The decomposition of [delta]-ferrite and austenitic grains occurs faster with increase in age-hardening temperature. Along with discontinuous decomposition of austenitic grains, there is a homogeneous (continuous) nucleation of Cr[2]N nitrides in those austenitic grains, which have not underwent discontinuous decomposition at the initial stages of aging. |
| Sprog: | russisk |
| Udgivet: |
2020
|
| Fag: | |
| Online adgang: | http://earchive.tpu.ru/handle/11683/62564 |
| Format: | MixedMaterials Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=631538 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 631538 | ||
| 005 | 20231102024535.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\33239 | ||
| 035 | |a RU\TPU\conf\33233 | ||
| 090 | |a 631538 | ||
| 100 | |a 20200908d2020 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Структурно-фазовые превращения в высокоазотистой Cr-Mn-N стали при старении |d Structural and phase transformations in a high-nitrogen Cr-Mn-N steel during aging |f И. А. Тумбусова, А. С. Михно |g науч. рук. Е. Г. Астафурова, Г. Г. Майер | |
| 203 | |a Текст |c электронный | ||
| 230 | |a 1 компьютерный файл (pdf; 1 054 Kb) | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 211 (2 назв.)] | ||
| 330 | |a In the present work, the structure and phase composition of a high nitrogen austenitic steel were studied in dependence on the aging temperature from 600°C to 800°C. Age-hardening in the regimes 600°С, 5 h., 700°С, 0,5 h., и 800°С, 10 min. is accompanied with a decomposition of a [delta]-ferrite into a [sigma]-phase and an austenite, and simulteneous discontinuous decomposition of austenite with the formation of Cr[2]N-cells along grain boundaries and cells of austenite depleted by interstitials. The decomposition of [delta]-ferrite and austenitic grains occurs faster with increase in age-hardening temperature. Along with discontinuous decomposition of austenitic grains, there is a homogeneous (continuous) nucleation of Cr[2]N nitrides in those austenitic grains, which have not underwent discontinuous decomposition at the initial stages of aging. | ||
| 338 | |b Российский научный фонд |d 17-19-01197 | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\32968 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XVII Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 21-24 апреля 2020 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2020 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\32969 |t Т. 1 : Физика |v [С. 209-211] |d 2020 | |
| 510 | 1 | |a Structural and phase transformations in a high-nitrogen Cr-Mn-N steel during aging |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a структурно-фазовые превращения | |
| 610 | 1 | |a высокоазотистые стали | |
| 610 | 1 | |a старение | |
| 610 | 1 | |a фазовый состав | |
| 610 | 1 | |a аустенитные стали | |
| 610 | 1 | |a границы зерен | |
| 700 | 1 | |a Тумбусова |b И. А. | |
| 701 | 1 | |a Михно |b А. С. | |
| 702 | 1 | |a Астафурова |b Е. Г. |c химик |c младший научный сотрудник Томского политехнического университета, кандидат физико-математических наук |f 1977- |g Елена Геннадьевна |2 stltpush |4 727 | |
| 702 | 1 | |a Майер |b Г. Г. |c специалист в области материаловедения |c младший научный сотрудник Томского политехнического университета |g Галина Геннадьевна |2 stltpush |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |c (2009- ) |2 stltpush |3 (RuTPU)RU\TPU\col\15902 |9 26305 |
| 801 | 2 | |a RU |b 63413507 |c 20200923 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/62564 | |
| 942 | |c BK | ||