Синтез и свойства биоактивных материалов на основе системы SiO[2]-P[2]O[5]-CaO-MgO; Перспективы развития фундаментальных наук; Т. 2 : Химия
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2018 Т. 2 : Химия.— 2018.— [С. 126-128] |
|---|---|
| Hovedforfatter: | |
| Institution som forfatter: | |
| Andre forfattere: | , |
| Summary: | Заглавие с экрана The article presents the results of synthesis and studies of the physico-chemical properties of biomaterials based on oxide system SiO[2]-P[2]O[5]-CaO-MgO. Solution with different contents of calcium and magnesium were prepared by the sol-gel method. Tetraethyl orthosilicate (TEOS), phosphoric acid (H[3]PO[4]), calcium nitrate (Ca(NO[3])[2]·4H[2]O) and magnesium nitrate (Mg(NO[3])[2]·6H[2]O) in ethanol (C[2]H[5]OH) were used for preparation of solution. Viscosity of the solutions was 1,72-1,82 mm{2}/s on the first day. Powder X-ray diffraction showed at 800°С in the samples fixed phases quartz SiO[2], whitlockite (Ca[2],589 Mg0,411 )(PO[4])2, [beta]-cristobalite high SiO[2], stanfieldite Mg[3]Ca[3](PO[4])[4]. Chemical bonds in the powders were identified by IR spectroscopy. The surface of the powders and chemical composition was investigated by SEM and EPMA. |
| Sprog: | russisk |
| Udgivet: |
2018
|
| Fag: | |
| Online adgang: | http://earchive.tpu.ru/handle/11683/50736 |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=627517 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 627517 | ||
| 005 | 20231101133451.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\27394 | ||
| 035 | |a RU\TPU\conf\27390 | ||
| 090 | |a 627517 | ||
| 100 | |a 20180911d2018 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Синтез и свойства биоактивных материалов на основе системы SiO[2]-P[2]O[5]-CaO-MgO |d Synthesis and properties of bioactive materials based on the system SiO[2]-P[2]O[5]-CaO-MgO |f Е. А. Изосимова, Е. С. Лютова |g науч. рук. Л. П. Борило | |
| 203 | |a Текст |c электронный | ||
| 230 | |a 1 компьютерный файл (pdf; 382 Kb) | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 128 (4 назв.)] | ||
| 330 | |a The article presents the results of synthesis and studies of the physico-chemical properties of biomaterials based on oxide system SiO[2]-P[2]O[5]-CaO-MgO. Solution with different contents of calcium and magnesium were prepared by the sol-gel method. Tetraethyl orthosilicate (TEOS), phosphoric acid (H[3]PO[4]), calcium nitrate (Ca(NO[3])[2]·4H[2]O) and magnesium nitrate (Mg(NO[3])[2]·6H[2]O) in ethanol (C[2]H[5]OH) were used for preparation of solution. Viscosity of the solutions was 1,72-1,82 mm{2}/s on the first day. Powder X-ray diffraction showed at 800°С in the samples fixed phases quartz SiO[2], whitlockite (Ca[2],589 Mg0,411 )(PO[4])2, [beta]-cristobalite high SiO[2], stanfieldite Mg[3]Ca[3](PO[4])[4]. Chemical bonds in the powders were identified by IR spectroscopy. The surface of the powders and chemical composition was investigated by SEM and EPMA. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\26928 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2018 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\26930 |t Т. 2 : Химия |v [С. 126-128] |d 2018 | |
| 510 | 1 | |a Synthesis and properties of bioactive materials based on the system SiO[2]-P[2]O[5]-CaO-MgO |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a синтез | |
| 610 | 1 | |a свойства | |
| 610 | 1 | |a биоактивные материалы | |
| 610 | 1 | |a медицинские исследования | |
| 610 | 1 | |a регенерация | |
| 610 | 1 | |a костные ткани | |
| 700 | 1 | |a Изосимова |b Е. А. | |
| 701 | 1 | |a Лютова |b Е. С. | |
| 702 | 1 | |a Борило |b Л. П. |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский государственный университет (ТГУ) |c (2009- ) |2 stltpush |3 (RuTPU)RU\TPU\col\17230 |
| 801 | 2 | |a RU |b 63413507 |c 20181005 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/50736 | |
| 942 | |c BK | ||