Физико-механические свойства нанокомпозитов на основе ZrO[2], армированных одностенными углеродными нанотрубками
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2018 Т. 1 : Физика.— 2018.— [С. 331-333] |
|---|---|
| Glavni avtor: | |
| Korporativna značnica: | |
| Drugi avtorji: | , |
| Izvleček: | Заглавие с экрана Zirconia ceramics reinforced with 0, 0.1, 0.5, and 1 wt.% single wall carbon nanotubes were fabricated by spark plasma sintering. The sintering was performed at 1500°C with a dwell time of 10 min, with heating and cooling rates of 100°C/min, and uniaxial pressure of 40 MPa was applied. Relative densities of the obtained pellets were calculated by weighing the pellets and measuring their dimensions. The highest value for microhardness was obtained for the pure ZrO[2] (14.72 GPa), and it decreased with the increase in the content of carbon nanotubes. On the other hand, fracture toughness of the obtained composites increased with the increase in carbon content. The highest value for fracture toughness was obtained for the composite with 1 wt.% of CNT (6.97 MPa·m{1/2}). |
| Jezik: | ruščina |
| Izdano: |
2018
|
| Teme: | |
| Online dostop: | http://earchive.tpu.ru/handle/11683/50679 |
| Format: | Elektronski Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=627465 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 627465 | ||
| 005 | 20231101133449.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\27326 | ||
| 035 | |a RU\TPU\conf\27222 | ||
| 090 | |a 627465 | ||
| 100 | |a 20180907d2018 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Физико-механические свойства нанокомпозитов на основе ZrO[2], армированных одностенными углеродными нанотрубками |d Physical and mechanical properties of ZrO[2]/single wall carbon nanotubes nanocomposites |f В. А. Цуканов, А. А. Леонов |g науч. рук. О. Л. Хасанов | |
| 203 | |a Текст |c электронный | ||
| 230 | |a 1 компьютерный файл (pdf; 619 Kb) | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 333 (5 назв.)] | ||
| 330 | |a Zirconia ceramics reinforced with 0, 0.1, 0.5, and 1 wt.% single wall carbon nanotubes were fabricated by spark plasma sintering. The sintering was performed at 1500°C with a dwell time of 10 min, with heating and cooling rates of 100°C/min, and uniaxial pressure of 40 MPa was applied. Relative densities of the obtained pellets were calculated by weighing the pellets and measuring their dimensions. The highest value for microhardness was obtained for the pure ZrO[2] (14.72 GPa), and it decreased with the increase in the content of carbon nanotubes. On the other hand, fracture toughness of the obtained composites increased with the increase in carbon content. The highest value for fracture toughness was obtained for the composite with 1 wt.% of CNT (6.97 MPa·m{1/2}). | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\26928 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2018 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\26929 |t Т. 1 : Физика |v [С. 331-333] |d 2018 | |
| 510 | 1 | |a Physical and mechanical properties of ZrO[2]/single wall carbon nanotubes nanocomposites |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a физико-механические свойства | |
| 610 | 1 | |a нанокомпозиты | |
| 610 | 1 | |a углеродные нанотрубки | |
| 610 | 1 | |a керамика | |
| 610 | 1 | |a спекание | |
| 610 | 1 | |a микротвердость | |
| 610 | 1 | |a армирование | |
| 700 | 1 | |a Цуканов |b В. А. | |
| 701 | 1 | |a Леонов |b А. А. |c специалист в области материаловедения |c специалист по учебно-методической работе Томского политехнического университета |f 1991- |g Андрей Андреевич |2 stltpush |3 (RuTPU)RU\TPU\pers\38520 | |
| 702 | 1 | |a Хасанов |b О. Л. |c физик, специалист в области наноматериалов |c профессор Томского политехнического университета, доктор технических наук |c директор Нано-Центра ТПУ, заведующий кафедрой наноматериалов и нанотехнологий |f 1958- |g Олег Леонидович |2 stltpush |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Отделение материаловедения |h 7871 |2 stltpush |3 (RuTPU)RU\TPU\col\23508 |
| 801 | 2 | |a RU |b 63413507 |c 20181005 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/50679 | |
| 942 | |c BK | ||