Влияние легирования водородом на структуру и микротвердость высокоазотистой стали, деформированной методом кручения под высоким давлением; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2018 Т. 1 : Физика.— 2018.— [С. 195-197] |
|---|---|
| Hovedforfatter: | |
| Institution som forfatter: | |
| Andre forfattere: | , , |
| Summary: | Заглавие с экрана The influence of hydrogen alloying on microstructure and microhardness of high-nitrogen Fe-19Cr21Mn-1.3V-0.8N-0.3C wt. % steel produced by high-pressure torsion (HPT) was investigated. Examination of Xrays diffraction data indicates that hydrogenation of HPT-processed specimens leads to a broadening of X-rays lines and their shifting as result of stacking-faults formation and high residual stresses. Hydrogenation of HPTprocessed steel promotes to gamma-epsilon martensitic transformation. Due to hydrogen-induced phase hardening, the microhardness of the steel increases from 6.5 GPa in hydrogen-free state to 6.8 GPa in hydrogencharged one. After exposure for 170 h. at air condition, the position of X-rays lines became close to one for state after HPT without hydrogen-charging due to release of hydrogen atoms. |
| Sprog: | russisk |
| Udgivet: |
2018
|
| Fag: | |
| Online adgang: | http://earchive.tpu.ru/handle/11683/50981 |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=627417 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 627417 | ||
| 005 | 20231101133448.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\27227 | ||
| 035 | |a RU\TPU\conf\27222 | ||
| 090 | |a 627417 | ||
| 100 | |a 20180905d2018 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние легирования водородом на структуру и микротвердость высокоазотистой стали, деформированной методом кручения под высоким давлением |d Influence of hydrogen alloying on structure and microhardness of highnitrogen steel deformed by high-pressure torsion |f Г. Г. Майер, Е. В. Мельников, В. А. Москвина |g науч. рук. Е. Г. Астафурова | |
| 203 | |a Текст |c электронный | ||
| 230 | |a 1 компьютерный файл (pdf; 343 Kb) | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 197 (4 назв.)] | ||
| 330 | |a The influence of hydrogen alloying on microstructure and microhardness of high-nitrogen Fe-19Cr21Mn-1.3V-0.8N-0.3C wt. % steel produced by high-pressure torsion (HPT) was investigated. Examination of Xrays diffraction data indicates that hydrogenation of HPT-processed specimens leads to a broadening of X-rays lines and their shifting as result of stacking-faults formation and high residual stresses. Hydrogenation of HPTprocessed steel promotes to gamma-epsilon martensitic transformation. Due to hydrogen-induced phase hardening, the microhardness of the steel increases from 6.5 GPa in hydrogen-free state to 6.8 GPa in hydrogencharged one. After exposure for 170 h. at air condition, the position of X-rays lines became close to one for state after HPT without hydrogen-charging due to release of hydrogen atoms. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\26928 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2018 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\26929 |t Т. 1 : Физика |v [С. 195-197] |d 2018 | |
| 510 | 1 | |a Influence of hydrogen alloying on structure and microhardness of highnitrogen steel deformed by high-pressure torsion |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a легирование | |
| 610 | 1 | |a водород | |
| 610 | 1 | |a структуры | |
| 610 | 1 | |a микротвердость | |
| 610 | 1 | |a высокоазотистые стали | |
| 610 | 1 | |a деформации | |
| 610 | 1 | |a кручения | |
| 610 | 1 | |a высокое давление | |
| 700 | 1 | |a Майер |b Г. Г. |c специалист в области материаловедения |c младший научный сотрудник Томского политехнического университета |g Галина Геннадьевна |2 stltpush |3 (RuTPU)RU\TPU\pers\30666 | |
| 701 | 1 | |a Мельников |b Е. В. | |
| 701 | 1 | |a Москвина |b В. А. | |
| 702 | 1 | |a Астафурова |b Е. Г. |c химик |c младший научный сотрудник Томского политехнического университета, кандидат физико-математических наук |f 1977- |g Елена Геннадьевна |2 stltpush |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Отделение материаловедения |h 7871 |2 stltpush |3 (RuTPU)RU\TPU\col\23508 |
| 801 | 2 | |a RU |b 63413507 |c 20181004 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/50981 | |
| 942 | |c BK | ||