Исследование водородостойкости, механических и трибологических свойств циркониевого сплава Э110 с покрытием нитрида титана, осажденного методом магнетронного распыления; Перспективы развития фундаментальных наук; Т. 1 : Физика
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2018 Т. 1 : Физика.— 2018.— [С. 162-164] |
|---|---|
| Autore principale: | |
| Ente Autore: | |
| Altri autori: | |
| Riassunto: | Заглавие с экрана In this paper, the increase in hydrogen resistance, mechanical and tribological properties of E110 alloy samples by TiN protective coating deposition under high-temperature gas-phase hydrogenation at 350° C, 450° C and 900° C was shown. The crystalline structure, surface morphology and depth distribution of elements were analyzed by X-ray diffraction, optical microscopy and glow-discharge optical emission spectroscopy, respectively. The intensity of hydrogen absorption by TiN-coated E110 alloy increases with hydrogenation temperature. Hardness and Young's modulus of the TiN coatings slightly changed under hydrogenation up to 450°C and dropped at 900°C. No cracks or delaminations were observed on the surface of TiN-coated samples after hydrogenation up to 450°C, however, the film was cracked after hydrogenation at 900° C. Evolution of friction coefficient of hydrogenated samples was shown. |
| Lingua: | russo |
| Pubblicazione: |
2018
|
| Soggetti: | |
| Accesso online: | http://earchive.tpu.ru/handle/11683/50969 |
| Natura: | MixedMaterials Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=627406 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 627406 | ||
| 005 | 20240119175207.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\27216 | ||
| 035 | |a RU\TPU\conf\27214 | ||
| 090 | |a 627406 | ||
| 100 | |a 20180905d2018 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Исследование водородостойкости, механических и трибологических свойств циркониевого сплава Э110 с покрытием нитрида титана, осажденного методом магнетронного распыления |d Hydrogen resistance, mechanical and tribological properties of zirconium alloy e110 with titanium nitride coating deposited by magnetron sputtering |f Э. М. Керимкулов |g науч. рук. Е. Б. Кашкаров | |
| 203 | |a Текст |c электронный | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 164 (3 назв.)] | ||
| 330 | |a In this paper, the increase in hydrogen resistance, mechanical and tribological properties of E110 alloy samples by TiN protective coating deposition under high-temperature gas-phase hydrogenation at 350° C, 450° C and 900° C was shown. The crystalline structure, surface morphology and depth distribution of elements were analyzed by X-ray diffraction, optical microscopy and glow-discharge optical emission spectroscopy, respectively. The intensity of hydrogen absorption by TiN-coated E110 alloy increases with hydrogenation temperature. Hardness and Young's modulus of the TiN coatings slightly changed under hydrogenation up to 450°C and dropped at 900°C. No cracks or delaminations were observed on the surface of TiN-coated samples after hydrogenation up to 450°C, however, the film was cracked after hydrogenation at 900° C. Evolution of friction coefficient of hydrogenated samples was shown. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\26928 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2018 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\26929 |t Т. 1 : Физика |v [С. 162-164] |d 2018 | |
| 510 | 1 | |a Hydrogen resistance, mechanical and tribological properties of zirconium alloy e110 with titanium nitride coating deposited by magnetron sputtering |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a водородоустойчивость | |
| 610 | 1 | |a механические свойства | |
| 610 | 1 | |a трибологические свойства | |
| 610 | 1 | |a циркониевые сплавы | |
| 610 | 1 | |a нитрид титана | |
| 610 | 1 | |a магнетронное распыление | |
| 610 | 1 | |a защитные покрытия | |
| 700 | 1 | |a Керимкулов |b Э. М. | |
| 702 | 1 | |a Кашкаров |b Е. Б. |c физик |c доцент, научный сотрудник Томского политехнического университета, кандидат физико-математических наук |f 1991- |g Егор Борисович |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Отделение экспериментальной физики |3 (RuTPU)RU\TPU\col\23549 |
| 801 | 2 | |a RU |b 63413507 |c 20181004 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/50969 | |
| 942 | |c BK | ||