Изменение структуры и фазового состава в материале сварного шва стали 12Х18Н10Т под действием пластической деформации
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2018 Т. 1 : Физика.— 2018.— [С. 30-32] |
|---|---|
| Corporate Authors: | , , , |
| Other Authors: | , , , |
| Summary: | Заглавие с экрана The paper presents the transmission electron microscopy (TEM) investigations of the structure and phase composition of the heat-affected zone (HAZ) in welded joint obtained by electrode welding. The type 12C 18Cr-10Ni-1Ti-Fe steel is used for welding which then subjected to plastic deformation. Quasi-static tensile tests are performed on a test machine Instron-1185. The acoustic emission and acoustic decay are respectively recorded and measured using the acoustic surface wave technique before and after the load application. TEM investigations are carried out within HAZ between the deposited and base metal at a 0,5 mm distance from the weld joint at 0, 5 and 37% deformation degrees. Thus, it is shown that in the area of the heat-affected zone, the plastic deformation leads to the martensite transformation as follows: [gamma->epsilon->alpha]. |
| Language: | Russian |
| Published: |
2018
|
| Subjects: | |
| Online Access: | http://earchive.tpu.ru/handle/11683/50707 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=627362 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 627362 | ||
| 005 | 20240110173921.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\27153 | ||
| 035 | |a RU\TPU\conf\27152 | ||
| 090 | |a 627362 | ||
| 100 | |a 20180903d2018 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Изменение структуры и фазового состава в материале сварного шва стали 12Х18Н10Т под действием пластической деформации |d Welding material structure and phase composition in 0.12C-18Cr-10Ni-1Ti-Fe steel modified by plastic deformation |f Н. В. Абабков [и др.] |g науч. рук. А. Н. Смирнов | |
| 203 | |a Текст |c электронный | ||
| 300 | |a Заглавие с экрана | ||
| 330 | |a The paper presents the transmission electron microscopy (TEM) investigations of the structure and phase composition of the heat-affected zone (HAZ) in welded joint obtained by electrode welding. The type 12C 18Cr-10Ni-1Ti-Fe steel is used for welding which then subjected to plastic deformation. Quasi-static tensile tests are performed on a test machine Instron-1185. The acoustic emission and acoustic decay are respectively recorded and measured using the acoustic surface wave technique before and after the load application. TEM investigations are carried out within HAZ between the deposited and base metal at a 0,5 mm distance from the weld joint at 0, 5 and 37% deformation degrees. Thus, it is shown that in the area of the heat-affected zone, the plastic deformation leads to the martensite transformation as follows: [gamma->epsilon->alpha]. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\26928 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 24-27 апреля 2018 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2018 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\26929 |t Т. 1 : Физика |v [С. 30-32] |d 2018 | |
| 510 | 1 | |a Welding material structure and phase composition in 0.12C-18Cr-10Ni-1Ti-Fe steel modified by plastic deformation |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a структуры | |
| 610 | 1 | |a фазовый состав | |
| 610 | 1 | |a сварные швы | |
| 610 | 1 | |a стали | |
| 610 | 1 | |a 12Х18Н10Т | |
| 610 | 1 | |a пластические деформации | |
| 610 | 1 | |a сварные соединения | |
| 701 | 1 | |a Абабков |b Н. В. | |
| 701 | 1 | |a Никоненко |b Е. Л. |c физик |c доцент Томского политехнического университета, кандидат физико-математических наук |f 1962- |g Елена Леонидовна |3 (RuTPU)RU\TPU\pers\35777 |9 18934 | |
| 701 | 1 | |a Попова |b Н. А. | |
| 701 | 1 | |a Смирнов |b А. Н. | |
| 702 | 1 | |a Смирнов |b А. Н. |4 727 | |
| 712 | 0 | 2 | |a Кузбасский государственный технический университет (КузГТУ) |c (Кемерово) |c (1993- ) |3 (RuTPU)RU\TPU\col\89 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский государственный университет (ТГУ) |c (2009- ) |3 (RuTPU)RU\TPU\col\17230 |
| 712 | 0 | 2 | |a Томский государственный архитектурно-строительный университет (ТГАСУ) |c (1997- ) |3 (RuTPU)RU\TPU\col\3 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |c (2009- ) |3 (RuTPU)RU\TPU\col\15902 |
| 801 | 2 | |a RU |b 63413507 |c 20181004 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/50707 | |
| 942 | |c BK | ||