Влияние оксида титана на свойства материалов, полученных из пленкообразующих растворов на основе системы SiO2-СаO-P2O5-TiO2; Перспективы развития фундаментальных наук; Т. 2 : Химия
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XIV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2017 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2017 Т. 2 : Химия.— 2017.— [С. 190-192] |
|---|---|
| Autor principal: | |
| Outros Autores: | , |
| Resumo: | Заглавие с экрана The sol-gel derived film-forming solutions (ERP) system based on SiO2‒CaO‒P2O5‒TiO2. After cooking the solution viscosity has a value of 2,65‒2,7 mm 2/s. In the first two days of maturation ERP test solutions pH values vary between 7,8‒7,7, and is positively charged colloidal particle according electrophoretic studies. Upon reaching values of solution viscosity of 3,8 mm2 /s pH in the system is reduced to 4. A colloidal particle has a negative charge during this period. After five days, the solutions are no longer suitable for the preparation of these high-quality films. Thin films obtained from the film forming solutions (ERP) on a substrate of monocrystalline silicon (substrate model) by centrifugation with a centrifuge speed of 3000 rev/min, followed by heat treatment at 60‒80 °C for 20 minutes and at 800 °C for 1 hour. With hydrodynamic traced main stages of oxide systems. For homogeneous material requires heat treatment at 800 °C. Biological activity was studied in vitro in the SBF medium. Increasing the titanium oxide in the system to 10 wt.%. Of the material is increased bioactivity. |
| Idioma: | russo |
| Publicado em: |
2017
|
| Assuntos: | |
| Acesso em linha: | http://earchive.tpu.ru/handle/11683/44520 |
| Formato: | Recurso Electrónico Capítulo de Livro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=624546 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 624546 | ||
| 005 | 20260812104708.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\23806 | ||
| 035 | |a RU\TPU\conf\23804 | ||
| 090 | |a 624546 | ||
| 100 | |a 20171123d2017 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние оксида титана на свойства материалов, полученных из пленкообразующих растворов на основе системы SiO2-СаO-P2O5-TiO2 |d Effect of titanium oxide on properties of materials, film-forming solution obtained from the system on the basis of SiO2-СаO-P2O5-TiO2 |f Е. С. Лютова, Л. Н. Спивакова |g науч. рук. Л. П. Борило | |
| 203 | |a Текст |c электронный | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 192 (2 назв.)] | ||
| 330 | |a The sol-gel derived film-forming solutions (ERP) system based on SiO2‒CaO‒P2O5‒TiO2. After cooking the solution viscosity has a value of 2,65‒2,7 mm 2/s. In the first two days of maturation ERP test solutions pH values vary between 7,8‒7,7, and is positively charged colloidal particle according electrophoretic studies. Upon reaching values of solution viscosity of 3,8 mm2 /s pH in the system is reduced to 4. A colloidal particle has a negative charge during this period. After five days, the solutions are no longer suitable for the preparation of these high-quality films. Thin films obtained from the film forming solutions (ERP) on a substrate of monocrystalline silicon (substrate model) by centrifugation with a centrifuge speed of 3000 rev/min, followed by heat treatment at 60‒80 °C for 20 minutes and at 800 °C for 1 hour. With hydrodynamic traced main stages of oxide systems. For homogeneous material requires heat treatment at 800 °C. Biological activity was studied in vitro in the SBF medium. Increasing the titanium oxide in the system to 10 wt.%. Of the material is increased bioactivity. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\21388 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XIV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2017 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2017 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\21390 |t Т. 2 : Химия |v [С. 190-192] |d 2017 | |
| 510 | 1 | |a Effect of titanium oxide on properties of materials, film-forming solution obtained from the system on the basis of SiO2-СаO-P2O5-TiO2 |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a синтез | |
| 610 | 1 | |a биоматериалы | |
| 610 | 1 | |a энергозатраты | |
| 610 | 1 | |a биосовместимость | |
| 610 | 1 | |a тонкопленочные материалы | |
| 700 | 1 | |a Лютова |b Е. С. | |
| 701 | 1 | |a Спивакова |b Л. Н. | |
| 702 | 1 | |a Борило |b Л. П. |4 727 | |
| 801 | 2 | |a RU |b 63413507 |c 20171206 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/44520 | |
| 942 | |c CF | ||