Получение пластин из молибдена и меди с помощью искрового плазменного спекания; Перспективы развития фундаментальных наук; Т. 2 : Химия
| Parent link: | Перспективы развития фундаментальных наук=Prospects of Fundamental Sciences Development: сборник научных трудов XIV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2017 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой.— , 2017 Т. 2 : Химия.— 2017.— [С. 214-216] |
|---|---|
| Hlavní autor: | |
| Korporativní autor: | |
| Další autoři: | , |
| Shrnutí: | Заглавие с экрана In the article, there has been molybdenum-copper bulk samples sintering, obtained the spark plasma sintering technology. XRD-diffraction, scanning electron microscopy and Vickers hardness test were carried out in this work. X-ray diffractometry analysis has shown that the products consist of the following main phases such as copper of cubic system (space group Fm-3m, No. 225) and molybdenum also of a cubic crystalline structure (space group Im3m, No. 229). Results of scanning electron microscopy for the sintered samples have shown that all bulk sintering samples have a high density. The optimal sintering temperature is 1060 oC. This is due to the fact that the bulk sample, sintered by 1060 oC, has a minimum amount of intergranular spaces. Vickers hardness test has shown that the highest hardness is 388 HV, at the same time hardness of pure molybdenum is 147 HV. |
| Jazyk: | ruština |
| Vydáno: |
2017
|
| Témata: | |
| On-line přístup: | http://earchive.tpu.ru/handle/11683/41365 |
| Médium: | Elektronický zdroj Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=622754 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 622754 | ||
| 005 | 20240123095431.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\21556 | ||
| 035 | |a RU\TPU\conf\21555 | ||
| 090 | |a 622754 | ||
| 100 | |a 20170707d2017 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Получение пластин из молибдена и меди с помощью искрового плазменного спекания |d Obtaining molybdenum-copper plates by spark pmasma sintering |f Ю. Н. Половинкина, Ю. Л. Шаненкова |g науч. рук. А. С. Ивашутенко | |
| 203 | |a Текст |c электронный | ||
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 216 (3 назв.)] | ||
| 330 | |a In the article, there has been molybdenum-copper bulk samples sintering, obtained the spark plasma sintering technology. XRD-diffraction, scanning electron microscopy and Vickers hardness test were carried out in this work. X-ray diffractometry analysis has shown that the products consist of the following main phases such as copper of cubic system (space group Fm-3m, No. 225) and molybdenum also of a cubic crystalline structure (space group Im3m, No. 229). Results of scanning electron microscopy for the sintered samples have shown that all bulk sintering samples have a high density. The optimal sintering temperature is 1060 oC. This is due to the fact that the bulk sample, sintered by 1060 oC, has a minimum amount of intergranular spaces. Vickers hardness test has shown that the highest hardness is 388 HV, at the same time hardness of pure molybdenum is 147 HV. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\conf\21388 |t Перспективы развития фундаментальных наук |l Prospects of Fundamental Sciences Development |o сборник научных трудов XIV Международной конференции студентов, аспирантов и молодых ученых, г. Томск, 25-28 апреля 2017 г. |o в 7 т. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. И. А. Курзиной, Г. А. Вороновой |d 2017 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\21390 |t Т. 2 : Химия |v [С. 214-216] |d 2017 | |
| 510 | 1 | |a Obtaining molybdenum-copper plates by spark pmasma sintering |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a терморегулирование | |
| 610 | 1 | |a электрические системы | |
| 610 | 1 | |a электронные приборы | |
| 610 | 1 | |a медь | |
| 610 | 1 | |a молибден | |
| 700 | 1 | |a Половинкина |b Ю. Н. |c специалист в области электроэнергетики и электротехники |c инженер Томского политехнического университета |f 1993- |g Юлия Николаевна |3 (RuTPU)RU\TPU\pers\45960 |9 22026 | |
| 701 | 1 | |a Шаненкова |b Ю. Л. |c специалист в области электроэнергетики |c доцент Томского политехнического университета, кандидат технических наук |f 1991- |g Юлия Леонидовна |3 (RuTPU)RU\TPU\pers\34117 |9 17657 | |
| 702 | 1 | |a Ивашутенко |b А. С. |c специалист в области электротехники |c заведующий кафедрой Томского политехнического университета, кандидат технических наук |f 1981- |g Александр Сергеевич |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Энергетический институт (ЭНИН) |b Кафедра электроснабжения промышленных предприятий (ЭПП) |3 (RuTPU)RU\TPU\col\18676 |
| 801 | 2 | |a RU |b 63413507 |c 20200129 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/41365 | |
| 942 | |c BK | ||