Влияние механоактивации на структуру хромоникелевой стали, полученной методом порошковой металлургии; Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2016.— [С. 97-99] |
|---|---|
| Autor principal: | |
| Autor Corporativo: | |
| Outros Autores: | , |
| Resumo: | Заглавие с титульного экрана This article presents research results of the chromium-nickel steel which was obtained by powder metallurgy. Powdered compositions were mechanical activated during 1 and 10 minutes. The aim of this investigation is analysis of the influence of mechanical activation on the structure and phase composition. Here it is shown that the sintered chromium-nickel steel has the austenitic-ferritic structure. Longer period mechanical action allows for a more homogeneous structure. |
| Idioma: | russo |
| Publicado em: |
2016
|
| Colecção: | Проблемы прочности, пластичности и усталостной долговечности современных конструкционных материалов |
| Assuntos: | |
| Acesso em linha: | http://earchive.tpu.ru/handle/11683/30992 |
| Formato: | Recurso Electrónico Capítulo de Livro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=619070 |
| Resumo: | Заглавие с титульного экрана This article presents research results of the chromium-nickel steel which was obtained by powder metallurgy. Powdered compositions were mechanical activated during 1 and 10 minutes. The aim of this investigation is analysis of the influence of mechanical activation on the structure and phase composition. Here it is shown that the sintered chromium-nickel steel has the austenitic-ferritic structure. Longer period mechanical action allows for a more homogeneous structure. |
|---|