Получение и свойства керамических материалов на основе системы Al[2]O[3]-MgO
| Parent link: | Материалы и технологии новых поколений в современном материаловедении: сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ). [С. 225-228].— , 2015 |
|---|---|
| Autore principale: | |
| Ente Autore: | |
| Altri autori: | |
| Riassunto: | Заглавие с титульного экрана It is known that aluminum oxide is the most generally used ceramic material applied as structural, functional and biomaterial. Meanwhile, it is used not only in a high state and but also in a highporous state. To obtain the required functional properties it is alloyed by various oxides such as FeO, SiO[2], Y[2]O[3], MgO and others. What most interested us is the magnasium oxide (MgO), as it is well known that the MgO presence in the ceramics materials causes biological processes activation at the boundary "implant - bone". However, the introduction of MgO into sintered mixture may change technological regimes of ceramics production and as a result to the structure and properties of the material can be changed as well. The aim of this work is to study the influence of the concentration of the injected mixture into the sintered MgO in the amount up to 10 wt. %. onto porosity, shrinkage characteristics of the microstructure and mechanical properties of the sintered material. |
| Pubblicazione: |
2015
|
| Serie: | Перспективные материалы и технологии |
| Soggetti: | |
| Accesso online: | http://earchive.tpu.ru/handle/11683/18275 http://www.lib.tpu.ru/fulltext/c/2015/C39/054.pdf |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616461 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 616461 | ||
| 005 | 20241121063150.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\14699 | ||
| 035 | |a RU\TPU\conf\14697 | ||
| 090 | |a 616461 | ||
| 100 | |a 20151228d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 105 | |a y z 101zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Получение и свойства керамических материалов на основе системы Al[2]O[3]-MgO |d Sintering and properties of alumina-magnesia ceramics |f К. Н . Куксина, С. П. Буякова | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Перспективные материалы и технологии | |
| 300 | |a Заглавие с титульного экрана | ||
| 330 | |a It is known that aluminum oxide is the most generally used ceramic material applied as structural, functional and biomaterial. Meanwhile, it is used not only in a high state and but also in a highporous state. To obtain the required functional properties it is alloyed by various oxides such as FeO, SiO[2], Y[2]O[3], MgO and others. What most interested us is the magnasium oxide (MgO), as it is well known that the MgO presence in the ceramics materials causes biological processes activation at the boundary "implant - bone". However, the introduction of MgO into sintered mixture may change technological regimes of ceramics production and as a result to the structure and properties of the material can be changed as well. The aim of this work is to study the influence of the concentration of the injected mixture into the sintered MgO in the amount up to 10 wt. %. onto porosity, shrinkage characteristics of the microstructure and mechanical properties of the sintered material. | ||
| 337 | |a Adobe Reader | ||
| 463 | 0 | |0 (RuTPU)RU\TPU\conf\14276 |t Материалы и технологии новых поколений в современном материаловедении |o сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ) |v [С. 225-228] |d 2015 | |
| 510 | 1 | |a Sintering and properties of alumina-magnesia ceramics |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a свойства | |
| 610 | 1 | |a керамические материалы | |
| 610 | 1 | |a оксиды алюминия | |
| 610 | 1 | |a биоматериалы | |
| 610 | 1 | |a порошки | |
| 610 | 1 | |a спеченные керамики | |
| 700 | 1 | |a Куксина |b К. Н . | |
| 701 | 1 | |a Буякова |b С. П. |g Светлана Петровна |c специалист в области материаловедения |c профессор Томского политехнического университета, доктор технических наук |f 1968- |y Томск |3 (RuTPU)RU\TPU\pers\28995 |9 13716 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра материаловедения в машиностроении (ММС) |3 (RuTPU)RU\TPU\col\18688 |
| 801 | 2 | |a RU |b 63413507 |c 20210209 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18275 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C39/054.pdf | |
| 942 | |c BK | ||