Влияние непрерывной и импульсной электронно-лучевой обработки на покрытие из хромованидиевого чугуна; Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2015.— [С. 164-168] |
|---|---|
| Autore principale: | |
| Ente Autore: | |
| Altri autori: | |
| Riassunto: | Заглавие с титульного экрана The paper reports the results of an investigation of structure formation in the eutectic chromium-vanadium cast iron coating deposited by electron-beam hardfacing (EBH) and subjected to multipoint pulsed electron-beam treatment (MPEBT) of the surface layers. The coating material structure in the zones modified by MPEBT changes considerably, showing the presence of a large amount of supersaturated austenite matrix and eutectic colonies in the form of fine isolated inclusions. The eutectic colonies are fan-like. The leading phase in the eutectic colonies is vanadium carbide. After aging within the temperature range from 900 to 1100°С the structure of the modified zones exhibits a large amount of fine secondary carbides Cr7C3 rejected from the matrix. The secondary carbides are uniformly distributed in the bulk of the modified zones. The matrix after aging undergoes [gamma]->[alpha] transformation and mainly has the martensitic structure. Aging increases significantly the hardness of the modified zones and abrasive wear resistance of the entire coating. |
| Lingua: | russo |
| Pubblicazione: |
2015
|
| Serie: | Поверхностное упрочнение и защитные покрытия |
| Soggetti: | |
| Accesso online: | http://earchive.tpu.ru/handle/11683/18263 http://www.lib.tpu.ru/fulltext/c/2015/C39/038.pdf |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616423 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 616423 | ||
| 005 | 20260622135836.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\14661 | ||
| 035 | |a RU\TPU\conf\14657 | ||
| 090 | |a 616423 | ||
| 100 | |a 20151225d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние непрерывной и импульсной электронно-лучевой обработки на покрытие из хромованидиевого чугуна |d Impact continuous and impulse electron beam processing to surface of chromium-vanadium cast iron |f А. М. Толстокулаков, Б. В. Дампилон | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Поверхностное упрочнение и защитные покрытия | |
| 300 | |a Заглавие с титульного экрана | ||
| 320 | |a [Библиогр.: с. 168 (4 назв.)] | ||
| 330 | |a The paper reports the results of an investigation of structure formation in the eutectic chromium-vanadium cast iron coating deposited by electron-beam hardfacing (EBH) and subjected to multipoint pulsed electron-beam treatment (MPEBT) of the surface layers. The coating material structure in the zones modified by MPEBT changes considerably, showing the presence of a large amount of supersaturated austenite matrix and eutectic colonies in the form of fine isolated inclusions. The eutectic colonies are fan-like. The leading phase in the eutectic colonies is vanadium carbide. After aging within the temperature range from 900 to 1100°С the structure of the modified zones exhibits a large amount of fine secondary carbides Cr7C3 rejected from the matrix. The secondary carbides are uniformly distributed in the bulk of the modified zones. The matrix after aging undergoes [gamma]->[alpha] transformation and mainly has the martensitic structure. Aging increases significantly the hardness of the modified zones and abrasive wear resistance of the entire coating. | ||
| 337 | |a Adobe Reader | ||
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\14276 |t Материалы и технологии новых поколений в современном материаловедении |o сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ) |v [С. 164-168] |d 2015 | |
| 510 | 1 | |a Impact continuous and impulse electron beam processing to surface of chromium-vanadium cast iron |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a импульсная обработка | |
| 610 | 1 | |a электронно-лучевая обработка | |
| 610 | 1 | |a покрытия | |
| 610 | 1 | |a чугун | |
| 610 | 1 | |a упрочненные детали | |
| 610 | 1 | |a электронно-лучевая наплавка | |
| 700 | 1 | |a Толстокулаков |b А. М. | |
| 701 | 1 | |a Дампилон |b Б. В. |c специалист в области материаловедения |c доцент Томского политехнического университета, кандидат технических наук |f 1977- |g Баир Вячеславович |3 (RuTPU)RU\TPU\pers\28241 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра материаловедения в машиностроении (ММС) |3 (RuTPU)RU\TPU\col\18688 |
| 801 | 2 | |a RU |b 63413507 |c 20210209 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18263 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C39/038.pdf | |
| 942 | |c BK | ||