Исследование влияния параметров наводороживания на скорость сорбции водорода циркониевым сплавом Э110 с нанесенным слоем никеля; Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2015.— [С. 128-131] |
|---|---|
| Autore principale: | |
| Ente Autore: | |
| Altri autori: | |
| Riassunto: | Заглавие с титульного экрана Investigation of temperature and pressure altering influence on hydrogen sorption rate of zirconium alloy E110 coated by nickel layer during hydrogenation at gas atmosphere was done in this work. It was shown that nickel coating on zirconium alloy results in significant hydrogen sorption rate increasing in temperature range 350 - 550 °С. The increasing of hydrogenation temperature from 350 °С to 550 °С at constant pressure 2 atm. leads to the hydrogen sorption rate increasing in 4.45 times for zirconium alloy coated by nickel layer. The increasing of hydrogenation pressure from 0.02 to 0.2 and from 0.2 to 2 atm. At constant temperature 550 °С leads to the hydrogen sorption rate increasing in 49.6 and 4.67 times respectively. |
| Lingua: | russo |
| Pubblicazione: |
2015
|
| Serie: | Поверхностное упрочнение и защитные покрытия |
| Soggetti: | |
| Accesso online: | http://earchive.tpu.ru/handle/11683/18257 http://www.lib.tpu.ru/fulltext/c/2015/C39/027.pdf |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616412 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 616412 | ||
| 005 | 20260622135224.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\14650 | ||
| 035 | |a RU\TPU\conf\14643 | ||
| 090 | |a 616412 | ||
| 100 | |a 20151225d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Исследование влияния параметров наводороживания на скорость сорбции водорода циркониевым сплавом Э110 с нанесенным слоем никеля |d Investigation of hydrogenation parameters influence on the hydrogen sorption rate of zirconium alloy E110 coated by nickel layer |f М. Н. Бабихина |g науч. рук. В. Н. Кудияров | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Поверхностное упрочнение и защитные покрытия | |
| 300 | |a Заглавие с титульного экрана | ||
| 320 | |a [Библиогр.: с. 131 (6 назв.)] | ||
| 330 | |a Investigation of temperature and pressure altering influence on hydrogen sorption rate of zirconium alloy E110 coated by nickel layer during hydrogenation at gas atmosphere was done in this work. It was shown that nickel coating on zirconium alloy results in significant hydrogen sorption rate increasing in temperature range 350 - 550 °С. The increasing of hydrogenation temperature from 350 °С to 550 °С at constant pressure 2 atm. leads to the hydrogen sorption rate increasing in 4.45 times for zirconium alloy coated by nickel layer. The increasing of hydrogenation pressure from 0.02 to 0.2 and from 0.2 to 2 atm. At constant temperature 550 °С leads to the hydrogen sorption rate increasing in 49.6 and 4.67 times respectively. | ||
| 337 | |a Adobe Reader | ||
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\14276 |t Материалы и технологии новых поколений в современном материаловедении |o сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ) |v [С. 128-131] |d 2015 | |
| 510 | 1 | |a Investigation of hydrogenation parameters influence on the hydrogen sorption rate of zirconium alloy E110 coated by nickel layer |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a наводороживание | |
| 610 | 1 | |a сорбция | |
| 610 | 1 | |a водород | |
| 610 | 1 | |a циркониевые сплавы | |
| 610 | 1 | |a слои | |
| 610 | 1 | |a никель | |
| 700 | 1 | |a Бабихина |b М. Н. | |
| 702 | 1 | |a Кудияров |b В. Н. |c физик |c инженер Томского политехнического университета |f 1990- |g Виктор Николаевич |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Физико-технический институт (ФТИ) |b Кафедра общей физики (ОФ) |3 (RuTPU)RU\TPU\col\18734 |
| 801 | 2 | |a RU |b 63413507 |c 20210209 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18257 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C39/027.pdf | |
| 942 | |c BK | ||