Структура и свойства защитных покрытий, полученных электронно-лучевой наплавкой композиционных СВС порошков "карбид титана - титан"; Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2015.— [С. 115-120] |
|---|---|
| Autor principal: | |
| Autor Corporativo: | |
| Resumo: | Заглавие с титульного экрана A structure of Ti-TiC coatings with different contents of titanium binder, overlaid of composite powders, which were obtained by self-propagating high-temperature synthesis, was investigated. The structure was studied by X-ray analysis and metallography. A size of the carbide particles in coatings, hardness of coatings and rate of wear were measured. |
| Idioma: | russo |
| Publicado em: |
2015
|
| Colecção: | Поверхностное упрочнение и защитные покрытия |
| Assuntos: | |
| Acesso em linha: | http://earchive.tpu.ru/handle/11683/18253 http://www.lib.tpu.ru/fulltext/c/2015/C39/024.pdf |
| Formato: | Recurso Electrónico Capítulo de Livro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616405 |
| Resumo: | Заглавие с титульного экрана A structure of Ti-TiC coatings with different contents of titanium binder, overlaid of composite powders, which were obtained by self-propagating high-temperature synthesis, was investigated. The structure was studied by X-ray analysis and metallography. A size of the carbide particles in coatings, hardness of coatings and rate of wear were measured. |
|---|