Влияние температуры нагружения на неупругие эффекты в двойном сплаве TI[49.2]NI[50.8](АТ. %); Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2015.— [С. 61-64] |
|---|---|
| Tác giả chính: | |
| Tác giả của công ty: | |
| Tác giả khác: | , |
| Tóm tắt: | Заглавие с титульного экрана The data about the supelasticity (SE) and shape memory effect (SME) under torsion of the samples of Ti[49.2]Ni[50.8](at. %) alloy after the isothermal loading inside the 285-346K temperature range are presented. The dependences of SE, SME and the plastic deformation (VS) the torsional strain under isothermal loading are obtained. The reversible martensitic deformation are analyzed using the idea about equivalent deformations under tension and torsion tests. The abnormally high recovery deformations exceeded the crystallography resource of recovery deformation (CRRD) about 4.5% was found after loading at 296K (below TR; TR is the temperature of the R phase formation ). The recovery deformations decrease to (or less) CRRD with the increase of loading temperature about 15-30 degree above TR. |
| Ngôn ngữ: | Tiếng Nga |
| Được phát hành: |
2015
|
| Loạt: | Проблемы прочности современных конструкционных материалов |
| Những chủ đề: | |
| Truy cập trực tuyến: | http://earchive.tpu.ru/handle/11683/18292 http://www.lib.tpu.ru/fulltext/c/2015/C39/013.pdf |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616392 |